公开(公告)号：KR1020110131717A

公开(公告)日：2011-12-07

申请号：KR1020100051297

申请日：2010-05-31

申请人： 주식회사 에스디비

发明人： 조헌영 ,  최정규 ,  고지호

IPC分类号： C09J175/04 ,  C09J11/02 ,  C08L75/04

CPC分类号： C09J175/04 ,  C08K5/10 ,  C08K5/16 ,  C09J11/06

摘要： PURPOSE: A moisture-curing(one pack type) polyurethane resin composition has good adhesiveness, short solidification time, excellent workability, little harmfulness for human body, and little effect of skin irritation or environmental hormone. CONSTITUTION: A moisture-curing(one pack type) polyurethane resin composition comprises a more than two functional isocyanate compound and polyol as active ingredients, and one or more components selected from chain extender, crosslinking agent, diluent, and catalyst. The more than two functional isocyanate compound is selected from toluene diisocyanate, diphenylmethane diisocyanate, polymeric diphenylmethane diisocyanate, tolidine diisocyanate, p-phenylene isocyanate, hexamethylene diisocyanate, hydrogenated diphenylmethane diisocyanate, and isophorone diisocyanate.

摘要翻译： 目的：湿润固化（一包型）聚氨酯树脂组合物具有良好的粘合性，凝固时间短，可加工性好，对人体的危害性小，皮肤刺激或环境激素影响小。 构成：一种湿固化（一包型）聚氨酯树脂组合物包含两种以上官能异氰酸酯化合物和多元醇作为活性成分，以及一种或多种选自扩链剂，交联剂，稀释剂和催化剂的组分。 多于两种官能异氰酸酯化合物选自甲苯二异氰酸酯，二苯基甲烷二异氰酸酯，聚合二苯基甲烷二异氰酸酯，甲苯胺二异氰酸酯，对亚苯基异氰酸酯，六亚甲基二异氰酸酯，氢化二苯甲烷二异氰酸酯和异佛尔酮二异氰酸酯。

公开(公告)号：KR101265239B1

公开(公告)日：2013-05-16

申请号：KR1020110008029

申请日：2011-01-27

申请人： 주식회사 에스디비

发明人： 조헌영 ,  최정규 ,  고지호 ,  최장민

IPC分类号： C04B41/50 ,  C09D1/02 ,  C04B28/24

摘要： 본발명은 -10℃에서도결빙하지않는수성의콘크리트표면강화제로서겨울철에도도포작업이가능하고, 알칼리규산염의화학반응에의해발현되는콘크리트표면강화효과는물론메틸규산칼륨(PMS)의화학반응에의한발수효과를동시에나타내는발수성과동결방지성을지닌수성알칼리규산염계콘크리트표면강화제와, 상기콘크리트표면강화제의제조방법및 상기콘크리트표면강화제를이용한콘크리트표면강화공법에관한것이다. 본발명에서개시하는콘크리트표면강화제는알칼리규산염과메틸규산칼륨을함유하기때문에콘크리트등의조직내에깊이침투하여규산염이콘크리트로부터유출되는 Ca등의다가금속이온과반응하여규산칼슘(또는금속)염을형성하여공극을충전하는동시에메틸규산칼륨이공기중의탄산가스와반응하여폴리메틸실리케이트를형성하여콘크리트조직내에서충전효과와발수성을부여하므로콘크리트구조물의방수성, 압출강도, 내마모성등의물성을크게향상시킬수 있다.

公开(公告)号：KR1020120086770A

公开(公告)日：2012-08-06

申请号：KR1020110008029

申请日：2011-01-27

申请人： 주식회사 에스디비

发明人： 조헌영 ,  최정규 ,  고지호 ,  최장민

IPC分类号： C04B41/50 ,  C09D1/02 ,  C04B28/24

CPC分类号： C04B41/50 ,  C04B14/045 ,  C04B22/062 ,  C04B22/10 ,  C04B2103/40

摘要： PURPOSE: An aqueous alkali silicate based surface reinforcing agent and a manufacturing method of the concrete surface reinforcing agent and a concrete surface reinforcing method using the same are provided to enhance penetrability and strong water repellency on concrete surface. CONSTITUTION: An aqueous alkali silicate based surface reinforcing agent comprises alkali silicate, potassium methyl silicate(PMS), a gelation time controlling agent and an anti-freezer. 2-20 weight% of methyl potassium silicate is included based on total weight of the concrete surface intensifier. 2-10 weight% of the gelation time controlling agent is included based on total weight of the concrete surface intensifier. 10-20 weight% of the anti-freezer is included based on total weight of the concrete surface intensifier. A manufacturing method of aqueous alkali silicate based concrete surface intensifier comprises the following steps: manufacturing aqueous solution by dissolving one of anti-freezer, a surface tension reducing agent, or a mixture thereof into distilled water; manufacturing a mixture by successively adding and stirring alkali silicate and methyl potassium silicate (PMS) into the solution; adding and stirring the gelation time controlling agent with the mixture; and filtering the solution.

摘要翻译： 目的：提供碱性硅酸盐水溶液表面增强剂和混凝土表面增强剂的制造方法以及使用其的混凝土表面增强方法，以增强混凝土表面的渗透性和强斥水性。 构成：含碱性硅酸盐的表面增强剂包括碱性硅酸盐，甲基硅酸钾（PMS），凝胶化时间控制剂和防冻剂。 基于混凝土表面增强剂的总重量，包括2-20重量％的甲基硅酸钾。 基于混凝土表面增强剂的总重量，包含2-10重量％的胶凝时间控制剂。 基于混凝土表面增强剂的总重量，包括10-20重量％的防冻器。 水性碱硅酸盐系混凝土表面增强剂的制造方法包括以下步骤：通过将抗冷冻剂，表面张力降低剂或其混合物中的一种溶解在蒸馏水中来制造水溶液; 通过将碱性硅酸盐和甲基硅酸钾（PMS）依次加入并搅拌，制成混合物; 用混合物加入并搅拌凝胶时间控制剂; 并过滤该解决方案。

公开(公告)号：KR101188321B1

公开(公告)日：2012-10-09

申请号：KR1020100051297

申请日：2010-05-31

申请人： 주식회사 에스디비

发明人： 조헌영 ,  최정규 ,  고지호

IPC分类号： C09J175/04 ,  C09J11/02 ,  C08L75/04

摘要： 본 발명은 습기경화형(1액형) 폴리우레탄 수지 조성물에 관한 것으로, 상기 조성물은 2 관능성 이상의 이소시아네이트 화합물과 폴리올을 유효성분으로 포함하여 구성되며, 상기에 더하여 접착성 및 기계적 물성을 증진시키기 위해 사슬연장제, 가교결합제, 희석제, 촉매 등을 포함하고, 또한 저장안정성 보강 및 증량 효과를 얻기 위해 기능성첨가제, 흡습제, 충전재 등을 더 포함할 수 있다.
본 발명에 따른 습기경화형(1액형) 폴리우레탄 수지 조성물은 접착력이 좋고, 고화시간이 짧으며, 작업성이 우수할 뿐만 아니라 약용제형으로서 인체에 유해성이 적고, 피부자극이나 환경호르몬에 의한 인체에 미치는 영향이 거의 없는 친환경성으로, 자동차, 항공기, 고속전철, 선박, 건축물, 주택 내장/바닥재용 탄성접착제, 건축용 도료, 접착제, 실링제(CAS) 등 여러 산업 분야에 적용 가능하다.