    바텀애쉬를 포함하는 내화 라이닝용 모르타르 조성물
    5.
    发明授权
    바텀애쉬를 포함하는 내화 라이닝용 모르타르 조성물 有权
    具有底部灰浆的摩擦组合物用于耐火衬里

    公开(公告)号：KR100671352B1

    公开(公告)日：2007-01-19

    申请号：KR1020050065163

    申请日：2005-07-19

    申请人： 주식회사 유니온 ,  삼성물산 주식회사

    发明人： 조남섭 ,  엄주일 ,  김건우 ,  이명섭 ,  박해균 ,  원종필 ,  김장호 ,  임윤묵

    IPC分类号： C04B18/06 ,  C04B14/02 ,  C04B16/06

    CPC分类号： Y02A30/248 ,  Y02W30/92

    摘要： A mortar composition for refractory lining with heat insulation, fire-proofing property and mechanical strength is provided to be employed in fabricating the refractory lining sufficient to prevent concrete explosion and collision of constructional structure during firing by reusing bottom-ash residual from fossil fuel used in a power plant as primary component of the mortar composition. The composition generally includes bottom ash as refractory aggregate. More particularly, the composition is formed by adding water to solid fraction comprising: 5-50wt.% of cement; 10-90wt.% of the bottom ash; 1-20wt.% of heat insulating aggregate; and 0.01-5wt.% of organic fiber. The cement is selected from typical Portland cement, white Portland cement, alumina cement, early strength Portland cement and high early strength cement. The solid fraction further includes 0.01 to 2wt.% of thickener agent which is selected from methyl cellulose or polyvinyl acetate, and/or 0.5 to 7wt% of accelerating agent.

    摘要翻译： 提供了一种用于耐火衬里的砂浆组合物，具有隔热，防火性能和机械强度，用于制造耐火材料衬里，足以防止混凝土爆炸和烧结期间结构结构的碰撞，通过重新使用来自化石燃料的底灰残余物 电厂是砂浆组成的主要组成部分。 组合物通常包括作为耐火骨料的底灰。 更具体地说，组合物是通过将水添加到固体部分而形成的，所述固体部分包括：5-50重量％的水泥; 10-90重量％的底灰; 1-20wt。％绝热骨料; 和0.01-5重量％的有机纤维。 水泥选自典型的波特兰水泥，白色波特兰水泥，氧化铝水泥，早期硅酸盐水泥和高强度水泥。 固体部分还包含0.01至2重量％的选自甲基纤维素或聚乙酸乙烯酯的增稠剂，和/或0.5至7重量％的促进剂。

    재생알루미나를 포함하는 내화 라이닝용 모르타르 조성물
    7.
    发明授权
    재생알루미나를 포함하는 내화 라이닝용 모르타르 조성물 有权
    用于回收衬里的回收氧化铝的MORTAR组合物

    公开(公告)号：KR100666083B1

    公开(公告)日：2007-01-09

    申请号：KR1020050065164

    申请日：2005-07-19

    申请人： 삼성물산 주식회사 ,  주식회사 유니온

    发明人： 박해균 ,  조남섭 ,  이명섭 ,  엄주일 ,  김건우 ,  원종필 ,  김장호 ,  임윤묵

    IPC分类号： C04B35/66 ,  C04B35/101

    摘要： A mortar composition containing recycled alumina from alumina waste of chemical or petroleum facilities is provided to be used for manufacturing refractory linings with desired mechanical strength and to give the linings with concrete explosion resistance and structure collision protection performances by primarily comprising the recycled alumina especially obtained from FCC catalyst waste. The composition includes recycled alumina prepared by heat treating waste alumina used in drying agent, adsorbent and/or catalyst carrier then discarded. The composition is prepared by adding solid fraction comprising: 5-50wt.% of cement; 10-80wt.% of the recycled alumina; 1-20wt.% of heat insulating aggregate; and 0.01-5wt.% or organic fiber to water. The cement is selected from typical Portland cement, white Portland cement, alumina cement, early strength Portland cement or high early strength cement. The heat insulating aggregate is recycled catalyst obtained by heat treating FCC catalyst waste.

    摘要翻译： 提供含有氧化铝废物化学或石油设施的回收氧化铝的砂浆组合物，用于制造具有所需机械强度的耐火材料衬里，并且通过主要包含回收的氧化铝给出具有混凝土抗爆性和结构碰撞保护性能的衬里， FCC催化剂废物。 该组合物包括通过热处理用于干燥剂，吸附剂和/或催化剂载体的废氧化铝制备的再循环氧化铝，然后丢弃。 通过加入固体成分制备组合物，该固体成分包含5-50重量％的水泥; 10-80重量％的回收氧化铝; 1-20wt。％绝热骨料; 和0.01-5重量％或有机纤维与水。 水泥选自典型的波特兰水泥，白色波特兰水泥，氧化铝水泥，早期硅酸盐水泥或高强度水泥。 绝热骨料是通过热处理FCC催化剂废料得到的回收催化剂。

    고순도 알루미나시멘트의 제조방법
    8.
    发明公开
    고순도 알루미나시멘트의 제조방법 有权
    制造高纯度氧化铝水泥的方法

    公开(公告)号：KR1019990065034A

    公开(公告)日：1999-08-05

    申请号：KR1019980000079

    申请日：1998-01-06

    申请人： 주식회사 유니온

    发明人： 문봉한 ,  조남섭 ,  엄주일

    IPC分类号： C04B7/32

    摘要： 본 발명은 고순도(Al
    2 O
    3 함량 65-75%) 알루미나시멘트를 제조하는 방법으로써, 100% 클링커(Clinker)의 분쇄 또는 고순도 소성알루미나의 첨가(0-10%)를 극소화시켜 내화물용 시멘트로서 우수한 물성을 기할 수 있는 고순도 알루미나시멘트의 제조방법에 관한 것으로, 원료로 CaCO
    3 함량이 90% 이상의 석회석과 Al
    2 O
    3 함량 95% 이상의 알루미나를 사용하고, Al
    2 O
    3 함량이 65-75%가 되도록 Al
    2 O
    3 /CaO 몰비를 1.1-1.5로 하며, 회전로에서 1400℃-1650℃로 소성하여 주광물이 CA(CaO·Al
    2 O
    3 ), 부광물이 CA
    2 (CaO·2Al
    2 O
    3 )인 것을 특징으로 하는 고순도 알루미나시멘트의 제조방법.

    고순도 알루미나시멘트의 제조방법
    9.
    发明授权
    고순도 알루미나시멘트의 제조방법 有权
    制造高纯度的氧化铝水泥的工艺

    公开(公告)号：KR100236556B1

    公开(公告)日：2000-03-02

    申请号：KR1019980000079

    申请日：1998-01-06

    申请人： 주식회사 유니온

    发明人： 문봉한 ,  조남섭 ,  엄주일

    IPC分类号： C04B7/32

    摘要： 본 발명은 고순도(Al
    2 O
    3 함량 65-75%) 알루미나시멘트를 제조하는 방법으로써, 100% 클링커(Clinker)의 분쇄 또는 고순도 소성알루미나의 첨가(0-10%)를 극소화시켜 내화물용 시멘트로서 우수한 물성을 기할 수 있는 고순도 알루미나시멘트의 제조방법에 관한 것으로, 원료로 CaCO
    3 함량이 90% 이상의 석회석과 Al
    2 O
    3 함량 95% 이상의 알루미나를 사용하고, Al
    2 O
    3 함량이 65-75%가 되도록 Al
    2 O
    3 /CaO 물비를 1.1-1.5로 하며, 회전로에서 1400℃-1650℃로 소성하여 주광물이 CA(CaO ·Al
    2 O
    3 ), 부광물이 CA
    2 (CaO ·2Al
    2 O
    3 )인 것을 특징으로 하는 고순도 알루미나시멘트의 제조방법.