公开(公告)号：US5122197A

公开(公告)日：1992-06-16

申请号：US573565

申请日：1990-08-28

申请人： Hiroshi Asai ,  Ichiro Kitayama ,  Kouji Mineshita ,  Ken Okazaki ,  Akira Ohtsuka ,  Yuichi Nishiyama ,  Yasuo Uosaki

发明人： Hiroshi Asai ,  Ichiro Kitayama ,  Kouji Mineshita ,  Ken Okazaki ,  Akira Ohtsuka ,  Yuichi Nishiyama ,  Yasuo Uosaki

IPC分类号： C22C37/06 ,  F16D69/02

CPC分类号： F16D69/027 ,  C22C37/06

摘要： A cast-iron product has a composition of 4.3-4.9 wt. % Carbon Equivalent (CE), 0.25-0.5 wt. % Chromium (Cr), 0.05-0.12 wt. % Tin (Sn), 0.4-1.2 wt. % Manganese (Mn), 0-0.1 wt. % Phosphorus (P), and 0-0.15 wt. % Sulfur (S), with the balance being Iron (Fe). A brake assembly comprises a sliding element made of such a cast iron, and the sliding element is adapted to slideably contact with a friction element or elements made of non-asbestos material and constitute the assembly. Further, a method of producing a cast iron product comprises the steps of casting a cast iron having a composition of 4.3-4.9 wt. % Carbon Equivalent (CE), 0.25-0.5 wt. % Chromium (Cr), 0.05-0.12 wt. % Tin (Sn), 0.4-1.2 wt. % Manganese (Mn), 0-0.1 wt. % Phosphorus (P), and 0-0.15 wt. % Sulfur (S), with the balance being Iron (Fe), releasing a mold at a temperature not less than A.sub.1 allotropic transformation temperature, and cooling the cast iron at a relatively high cooling rate.

摘要翻译： 铸铁产品的组成为4.3-4.9wt。 ％碳当量（CE），0.25-0.5重量％ ％铬（Cr），0.05-0.12重量％ ％锡（Sn），0.4-1.2重量％ ％锰（Mn），0-0.1重量％ 磷（P）和0-0.15重量％ ％硫（S），余量为铁（Fe）。 制动组件包括由这种铸铁制成的滑动元件，并且滑动元件适于与由非石棉材料制成的摩擦元件滑动接触并构成组件。 此外，制造铸铁制品的方法包括以下步骤：铸造组成为4.3-4.9重量％的铸铁。 ％碳当量（CE），0.25-0.5重量％ ％铬（Cr），0.05-0.12重量％ ％锡（Sn），0.4-1.2重量％ ％锰（Mn），0-0.1重量％ 磷（P）和0-0.15重量％ ％硫（S），余量为铁（Fe），在不低于A1同素异形转变温度的温度下释放模具，并以相对较高的冷却速度冷却铸铁。