公开(公告)号：US20230167557A1

公开(公告)日：2023-06-01

申请号：US18095520

申请日：2023-01-10

Applicant: ArcelorMittal

Inventor： Thomas HENRION ,  Ronan JACOLOT ,  Martin BEAUVAIS

IPC: C23C28/02 ,  C22C33/04 ,  C22C38/58 ,  C22C38/54 ,  C22C38/50 ,  C22C38/48 ,  C22C38/44 ,  C22C38/06 ,  C22C38/04 ,  C22C38/02 ,  C22C38/00 ,  C21D7/13 ,  B32B15/01

CPC classification number: C23C28/025 ,  C22C33/04 ,  C22C38/58 ,  C22C38/54 ,  C22C38/50 ,  C22C38/48 ,  C22C38/44 ,  C22C38/06 ,  C22C38/04 ,  C22C38/02 ,  C22C38/002 ,  C22C38/001 ,  C21D7/13 ,  B32B15/016

Abstract: A method for manufacturing a hot-rolled and coated steel sheet having a thickness between 1.8 mm and 5 mm. The method contains the steps of: providing a semi-product having a composition containing: 0.04%≤C≤0.38%, 0.40%≤Mn≤3%, 0.005%≤Si≤0.70%, 0.005%≤Al≤0.1%, 0.001%≤Cr≤2%, 0.001%≤Ni≤2%, 0.001%≤Ti≤0.2%, Nb≤0.1%, B≤0.010%, 0.0005%≤N≤0.010%, 0.0001%≤S≤0.05%, 0.0001%≤P≤0.1%, Mo≤0.65%, W≤0.30%, Ca≤0.006%, hot-rolling with a final rolling temperature FRT, to obtain a hot-rolled steel product having a thickness between 1.8 mm and 5 mm, then cooling down to a coiling temperature Tcoil satisfying: 450° C.≤Tcoil≤Tcoilmax with Tcoilmax=650−140×fγ, Tcoilmax being expressed in degrees Celsius and fγ designating the austenite fraction just before the coiling, and coiling to obtain a hot-rolled steel substrate, pickling and coating the hot-rolled steel substrate with Al or an Al alloy by continuous hot-dipping in a bath, to obtain a hot-rolled and coated steel sheet containing a hot-rolled steel sheet and an Al or an Al alloy coating, having a thickness between 10 and 33 μm, on each side of the hot-rolled steel sheet.

公开(公告)号：US20200224297A1

公开(公告)日：2020-07-16

申请号：US16349864

申请日：2017-11-23

Applicant: ArcelorMittal

Inventor： Thomas HENRION ,  Ronan JACOLOT ,  Martin BEAUVAIS

IPC: C22C38/50 ,  C22C38/48 ,  C22C38/02 ,  C22C38/04 ,  C21D8/02 ,  C23C2/12 ,  B21D22/02 ,  C23C2/40

Abstract: A method for manufacturing a hot-rolled and coated steel sheet having a thickness between 1.8 mm and 5 mm. The method contains the steps of: providing a semi-product having a composition containing: 0.04%≤C≤0.38%, 0.40%≤Mn≤3%, 0.005%≤Si≤0.70%, 0.005%≤Al≤0.1%, 0.001%≤Cr≤2%, 0.001%≤Ni≤2%, 0.001%≤Ti≤0.2%, Nb≤0.1%, B≤0.010%, 0.0005%≤N≤0.010%, 0.0001%≤S≤0.05%, 0.0001%≤P≤0.1%, Mo≤0.65%, W≤0.30%, Ca≤0.006%, hot-rolling with a final rolling temperature FRT, to obtain a hot-rolled steel product having a thickness between 1.8 mm and 5 mm, then cooling down to a coiling temperature Tcoil satisfying: 450° C.≤Tcoil≤Tcoilmax with Tcoilmax=650−140×fγ, Tcoilmax being expressed in degrees Celsius and fγ designating the austenite fraction just before the coiling, and coiling to obtain a hot-rolled steel substrate, pickling and coating the hot-rolled steel substrate with Al or an Al alloy by continuous hot-dipping in a bath, to obtain a hot-rolled and coated steel sheet containing a hot-rolled steel sheet and an Al or an Al alloy coating, having a thickness between 10 and 33 μm, on each side of the hot-rolled steel sheet.