公开(公告)号：US08748524B2

公开(公告)日：2014-06-10

申请号：US13272306

申请日：2011-10-13

申请人： Bjorn Egeland ,  Alf Håberg ,  Johan Arnold Johansen ,  Stian Madshus

发明人： Bjorn Egeland ,  Alf Håberg ,  Johan Arnold Johansen ,  Stian Madshus

IPC分类号： C09J171/14 ,  C09J161/06 ,  C08K3/14 ,  C08K3/34

CPC分类号： C04B37/005 ,  C04B35/6264 ,  C04B35/62685 ,  C04B35/63476 ,  C04B37/008 ,  C04B2235/6562 ,  C04B2235/6565 ,  C04B2235/6567 ,  C04B2237/083 ,  C04B2237/16 ,  C04B2237/341 ,  C04B2237/363 ,  C04B2237/365 ,  C04B2237/368 ,  C04B2237/76 ,  C08K3/14 ,  C08K3/34 ,  C08K2003/023 ,  C09J161/06 ,  C09J171/14

摘要： The present invention relates to a heat crucible glue or coating for use in connection with refractory materials and ceramics. The glue or coating comprises 25 to 50 weight % silicon powder, 5 to 20 weight % SiC powder, 20 to 60 weight % formaldehyde resin or polyfurfuryl alcohol and 10 to 30 weight % of an organic solvent.

摘要翻译： 本发明涉及一种与难熔材料和陶瓷结合使用的热坩埚胶或涂层。 胶或涂层包含25至50重量％的硅粉末，5至20重量％的SiC粉末，20至60重量％的甲醛树脂或聚糠醇和10至30重量％的有机溶剂。

公开(公告)号：US20130004410A1

公开(公告)日：2013-01-03

申请号：US13574101

申请日：2011-01-18

申请人： Johan Arnold Johansen ,  Sten Yngve Larsen ,  Hermann Gran

发明人： Johan Arnold Johansen ,  Sten Yngve Larsen ,  Hermann Gran

IPC分类号： C01B31/04

CPC分类号： C25C3/08 ,  C04B35/522 ,  C04B35/532 ,  C04B2235/656 ,  C04B2235/722 ,  C04B2235/726 ,  C04B2235/77 ,  C25C7/02

摘要： The present invention relates to a method for production of graphite bodies. Carbon bodies are formed from a mixture of electric calcined coke particles calcined at a temperature between 1200 and 3000° C. and a binder where the coke particles have sulphur-and nitrogen content varying between 0 and 1.5% by weight and where the coke particles have an average sulphur content less than 0.6% by weight and a nitrogen content of less than 0.6% by weight, baking of the carbon bodies at a temperature between 700 and 1400° C. and graphitizing of the baked carbon bodies at a temperature above 2300° C.

摘要翻译： 本发明涉及石墨体的制造方法。 碳体由在1200和3000℃之间煅烧的电煅烧焦炭颗粒的混合物和粘合剂形成，其中焦炭颗粒的硫和氮含量在0和1.5重量％之间变化，并且焦炭颗粒具有 平均硫含量小于0.6重量％，氮含量小于0.6重量％，碳体在700〜1400℃的温度下焙烧，焙烧碳体在2300度以上的石墨化 C。