公开(公告)号：US20090170005A1

公开(公告)日：2009-07-02

申请号：US12092166

申请日：2006-10-31

申请人： Kotaro Kimishima ,  Norimitsu Kaimai

发明人： Kotaro Kimishima ,  Norimitsu Kaimai

IPC分类号： H01M2/16

CPC分类号： H01M2/1653 ,  H01M2/145 ,  H01M2/348 ,  H01M10/0565 ,  H01M2300/0082

摘要： A microporous polyolefin membrane made of a polyethylene resin as a main component, and having (a) a shutdown temperature of 135° C. or lower, at which the air permeability measured while heating at a temperature-elevating speed of 5° C./minute reaches 1×105 sec/100 cm3, (b) an air permeability change ratio of 1×104 sec/100 cm3/° C. or more, which is a gradient of a curve representing the dependency of the above air permeability on a temperature at the air permeability of 1×104 sec/100 cm3, and (c) a meltdown temperature of 150° C. or higher, at which the air permeability measured while further heating after reaching the above shutdown temperature becomes 1×105 sec/100 cm3 again.

摘要翻译： 一种由聚乙烯树脂作为主要成分制成的微孔聚烯烃膜，其特征在于，（a）在温度升高速度为5℃的同时测定的透气度为135℃以下的关闭温度。 分钟达到1×10 5秒/ 100cm 3，（b）1×104秒/ 100cm 3 /℃以上的透气度变化率，其为表示上述透气度对空气温度的依赖性的曲线的梯度 渗透率为1×104秒/ 100cm 3，（c）在达到上述关闭温度后进一步加热时测得的透气度再次为1×10 5秒/ 100cm 3的熔融温度为150℃以上。

公开(公告)号：US20070128512A1

公开(公告)日：2007-06-07

申请号：US10596171

申请日：2004-12-02

申请人： Norimitsu Kaimai ,  Shigeaki Kobayashi ,  Kotaro Kimishima ,  Sadakatsu Suzuki ,  Satoshi Ueki ,  Kazuhiro Yamada

发明人： Norimitsu Kaimai ,  Shigeaki Kobayashi ,  Kotaro Kimishima ,  Sadakatsu Suzuki ,  Satoshi Ueki ,  Kazuhiro Yamada

IPC分类号： H01M2/16 ,  H01M2/18 ,  B32B27/08

CPC分类号： B32B15/085 ,  B01D69/12 ,  B01D69/125 ,  B01D71/26 ,  B01D2325/20 ,  B01D2325/34 ,  B32B5/18 ,  B32B15/20 ,  B32B27/32 ,  B32B2305/026 ,  B32B2457/10 ,  H01M2/0222 ,  H01M2/1653 ,  Y10T428/249993 ,  Y10T428/31913

摘要： A microporous composite membrane comprising a microporous polyolefin membrane and a polypropylene-based coating layer formed on at least one surface of the microporous polyolefin membrane, the polypropylene having a mass-average molecular weight within a range of 5,000-500,000, and solubility of 0.5 g or more in 100 g of toluene at a temperature of 25° C., and the microporous composite membrane having air permeability (converted to the value at 25-μm thickness) of 50-10,000 seconds/100 cc.

摘要翻译： 一种微孔复合膜，其包含微孔聚烯烃膜和形成在所述微孔聚烯烃膜的至少一个表面上的聚丙烯基涂层，所述聚丙烯的质均分子量在5,000-500,000范围内，溶解度为0.5g 以上，在温度25℃的甲苯100g中，具有50-10,000秒/ 100cc透气度（25μm厚的值）的微孔复合膜。