公开(公告)号：US5169811A

公开(公告)日：1992-12-08

申请号：US643255

申请日：1991-01-22

申请人： Ned E. Cipollini ,  Beili L. Wu ,  Stephen Haig ,  Jean Yamanis

发明人： Ned E. Cipollini ,  Beili L. Wu ,  Stephen Haig ,  Jean Yamanis

IPC分类号： C01G37/00 ,  C04B35/42 ,  C04B35/50 ,  C04B35/624 ,  H01M8/02 ,  H01M8/12

CPC分类号： H01M8/0215 ,  C01G37/006 ,  C04B35/42 ,  C04B35/624 ,  H01M8/1213 ,  C01P2002/02 ,  C01P2002/54 ,  C01P2006/10 ,  C01P2006/12 ,  H01M2008/1293 ,  H01M2300/0074

摘要： A lanthanum chromite ceramic powder mixture that consists essentially of 1 mol of LaCr.sub.1-x M.sub.x O.sub.3, where M is a divalent metal selected from the group consisting of magnesium, calcium and mixtures thereof and x ranges from 0.03 to 0.3; y mols of B.sub.2 O.sub.3, where y ranges from 0.005 to 0.04; and z mols of La.sub.2 O.sub.3, where the ratio z/y ranges from 1.1 to 3. The mixture is formed into powder compacts and sintered to near full density at temperatures as low as 1400.degree. C.

摘要翻译： 基本上由1mol LaCr1-xMxO3组成的亚铬酸镧陶瓷粉末混合物，其中M是选自镁，钙及其混合物的二价金属，x在0.03至0.3的范围内; B2O3的摩尔数，其中y为0.005至0.04; 和zmol的La 2 O 3，其中z / y的比率为1.1至3.将混合物形成粉末压块并在低至1400℃的温度下烧结至接近全密度。