公开(公告)号：US4661171A
公开(公告)日：1987-04-28
申请号：US768716
申请日：1985-08-23
摘要： This disclosure is concerned with a method for treating a stainless steel surface by high temperature oxidation. The surface of a stainless steel article is cleaned. TiO.sub.2 and SiO.sub.2 are mixed in microparticles to form a coating agent, and water is added to the mixture to make a slip. The slip is coated on the steel surface to form a coating having a uniform thickness. The coating is dried and the article is subjected to a heat-treatment to form an oxide film. This treatment is performed in an oxidizing atmosphere for a time and a temperature suitable for the color tone to be produced. A desirable temperature for the heat-treatment is between 350.degree. C. to 700.degree. C. When a coating agent is used, it is later removed by washing, etc. after cooling the article.Further, when less dissolution of iron from the stainless steel surface is required, a decolorization treatment is applied; that is, the colored oxide film is removed from the surface by dissolution using an acid or an electrolytic treatment.
-
2.发明授权Method for treating the surface of stainless steel by high temperature oxidation 失效通过高温氧化处理不锈钢表面的方法
公开(公告)号：US4776897A
公开(公告)日：1988-10-11
申请号：US928783
申请日：1986-11-10
摘要： This disclosure is concerned with a method for treating a stainless steel surface by high temperature oxidation. The surface of a stainless steel article is cleaned, TiO.sub.2 and SiO.sub.2 are mixed in microparticles to form a coating agent, and water is added to the mixture to make a slip. The slip is coated on the steel surface to form a coating having a uniform thickness. The coating is dried and the article is subjected to a heat-treatment to form an oxide film. This treatment is performed in an oxidizing atmosphere for a time and a temperature suitable for the color tone to be produced. A desirable temperature for the heat-treatment is between 350.degree. C. to 700.degree. C. When a coating agent is used, it is later removed by washing, etc. after cooling the article. Further, when less dissolution of iron from the stainless steel surface is required, a decolorization treatment is applied; that is, the colored oxide film is removed from the surface by dissolution using an acid or an electrolytic treatment.
-
搜索结果
2 条记录 (耗时 0.009 秒)