摘要： A process for making epoxy resin foam blocks of varying density comprising mixing together (i) a foam resin comprising: a first epoxy resin, a foaming agent to the extent of 2% to 10% of the mass of the epoxy resin, a surfactant to the extent of 2% to 6% of the mass of the epoxy resin, a filler, a toughening agent and (ii) a curing agent comprising: a hardener and a second epoxy resin, the ratio of the foam resin to curing agent being in the range of about 100:20 to 100:25 by mass to form a reaction mixture; pouring the reaction mixture inside a mold maintained at a temperature in the range of 70° to 80° C. and allowing the mixture to cure in the mold for 60 to 100 min.; allowing the mold to cool at a temperature in the range of 15° C. to 30° C. and demolding to obtain a green block; and post-curing the green block in an air circulatory oven for 10 to 15 hrs to obtain a final hard foam block.

摘要翻译： 一种制备具有不同密度的环氧树脂泡沫块的方法，包括将（i）泡沫树脂混合在一起（i）泡沫树脂，其包含：第一环氧树脂，发泡剂至环氧树脂质量的2％至10％的程度， 环氧树脂，填料，增韧剂的质量的2％至6％的程度和（ii）固化剂，其包含：固化剂和第二环氧树脂，泡沫树脂与固化剂的比例为 的范围为约100:20至100:25，以形成反应混合物; 将反应混合物倒入保持在70℃至80℃范围内的模具中，并使混合物在模具中固化60至100分钟; 允许模具在15℃至30℃的温度下冷却并脱模以获得绿色块; 并在空气循环烘箱中将绿色块后固化10至15小时以获得最终的硬泡沫块。

公开(公告)号：US20110042843A1

公开(公告)日：2011-02-24

申请号：US12810243

申请日：2008-10-21

申请人： Amit Dixit ,  Pradip Kumar Dubey ,  Tatiya Laksanangam

发明人： Amit Dixit ,  Pradip Kumar Dubey ,  Tatiya Laksanangam

IPC分类号： C08J9/228

CPC分类号： C08J9/06 ,  C08J2363/00

摘要： A process for making epoxy resin foam blocks of varying density comprising mixing together (i) a foam resin comprising: a first epoxy resin, a foaming agent to the extent of 2% to 10% of the mass of the epoxy resin, a surfactant to the extent of 2% to 6% of the mass of the epoxy resin, a filler, a toughening agent and (ii) a curing agent comprising: a hardener and a second epoxy resin, the ratio of the foam resin to curing agent being in the range of about 100:20 to 100:25 by mass to form a reaction mixture; pouring the reaction mixture inside a mold maintained at a temperature in the range of 70° to 80° C. and allowing the mixture to cure in the mold for 60 to 100 min.; allowing the mold to cool at a temperature in the range of 15° C. to 30° C. and demolding to obtain a green block; and post-curing the green block in an air circulatory oven for 10 to 15 hrs to obtain a final hard foam block.

摘要翻译： 一种制备具有不同密度的环氧树脂泡沫块的方法，包括将（i）泡沫树脂混合在一起（i）泡沫树脂，其包含：第一环氧树脂，发泡剂至环氧树脂质量的2％至10％的程度， 环氧树脂，填料，增韧剂的质量的2％至6％的程度和（ii）固化剂，其包含：固化剂和第二环氧树脂，泡沫树脂与固化剂的比例为 的范围为约100:20至100:25，以形成反应混合物; 将反应混合物倒入保持在70℃至80℃范围内的模具中，并使混合物在模具中固化60至100分钟; 允许模具在15℃至30℃的温度下冷却并脱模以获得绿色块; 并在空气循环烘箱中将绿色块后固化10至15小时以获得最终的硬泡沫块。