摘要:
A process for the manufacture of acicular ferrimagnetic iron oxide by converting acicular iron(III) oxide hydroxide at from 300.degree. to 650.degree. C., by treatment with an organic compound which decomposes in this temperature range in the presence of iron oxide, the iron(III) oxide hydroxide used for the reaction being a lepidocrocite which has been heat-treated at from 300.degree. to 700.degree. C.
摘要:
A process for the manufacture of acicular ferrimagnetic iron oxide by reducing heat-treated acicular iron(III) oxide hydroxide with an organic compound which decomposes in the presence of iron oxide at from 450.degree. to 650.degree. C., followed by at least partial oxidation with an oxygen-containing gas at from 200.degree. to 500.degree. C., wherein the iron(III) oxide hydroxide employed is heat-treated at from 450.degree. to 700.degree. C. and has a surface area, measured by the BET method, of from 10 to 23 m.sup.2 /g.
摘要:
A process for the manufacture of acicular ferromagnetic iron particles by reducing an iron(III) oxide which carries a shape-stabilizing surface coating and has been produced by heating acicular iron(III) oxide hydroxide at 250.degree.-390.degree. C. in an atmosphere containing water vapor at a partial pressure of not less than 30 mbar, with hydrogen at 275.degree.-425.degree. C.
摘要:
A process for the manufacture of acicular ferrimagnetic iron oxide by heating iron(III) oxide or iron(III) oxide hydroxide at 220.degree.-460.degree. C. under a water vapor partial pressure of not less than 30 mbar, reducing the resulting product to magnetite by means of hydrogen and/or CO and/or an organic compound which can decompose in the presence of iron oxide, and then oxidizing the magnetite with an oxygen-containing gas to give acicular ferrimagnetic iron oxide of the formula FeO.sub.X, where X is from 1.33 to 1.50.
摘要:
A process for the preparation of acicular gamma-iron(III) oxide of high coercive force by reducing acicular iron(III) oxide hydroxide, as it is being passed continuously through a furnace having two or more heating zones at from 190.degree. to 700.degree. C., by means of a gas mixture which is produced by passing a stream of inert gas, heated to above 250.degree. C., through an organic substance also heated to above 250.degree. C. in a vessel, and, on introduction into the furnace, is first brought into contact with the .alpha.-iron(III) oxide formed from the iron(III) oxide hydroxide by elimination of water in the first heating zone of the furnace at from 190.degree. to 250.degree. C., the .alpha.-iron(III) oxide thereby being converted to magnetite which is subsequently oxidized with an oxygen-containing gas at from 150.degree. to 400.degree. C., to give gamma-iron(III) oxide.
摘要:
A process for the preparation of acicular ferromagnetic metal particles, consisting essentially of iron, by reducing acicular iron oxides and/or iron oxide hydroxides, which are either pure or are modified with conventional foreign metal ions, by means of a gaseous reducing agent in a fluidized bed furnace in which a stirrer is provided immediately above the fluidizing grid.