    HIGH TRANSMITTANCE LIGHT-COLORED GLASS AND PROCESS FOR PRODUCING THE GLASS
    3.
    发明申请
    HIGH TRANSMITTANCE LIGHT-COLORED GLASS AND PROCESS FOR PRODUCING THE GLASS 审中-公开
    高透光度的有色玻璃和生产玻璃的方法

    公开(公告)号：US20120135851A1

    公开(公告)日：2012-05-31

    申请号：US13367828

    申请日：2012-02-07

    申请人： Shoshiro OKADA ,  Shuichi Akada

    发明人： Shoshiro OKADA ,  Shuichi Akada

    IPC分类号： C03C3/095

    CPC分类号： C03C3/095 ,  C03C4/0092 ,  C03C4/02

    摘要： To provide a high transmittance light-colored glass having a high Tva (at least 60%), a low Te (at most 60%), a low Pe (at most 6.0%) and λd of from 560 to 780 nm or λc of from −550 to −492 nm. A high transmittance light-colored glass comprising, as a glass matrix composition, SiO2: from 63 to 75 mass %, Al2O3: from 0 to 5 mass %, Na2O: from 5 to 15 mass %, K2O: from 0 to 5 mass %, CaO: from 5 to 15 mass %, and MgO: from 0 to 10 mass %, and as coloring components, Er2O3: from 0.3 to 3.0 mass %, t-Fe2O3: from 0.05 to 0.5 mass %, and Se: from 1 to 30 ppm, and having Redox: more than 62%.

    摘要翻译： 为了提供具有高Tva（至少60％），低Te（至多60％），低Pe（至多6.0％）和λd为560至780nm或λc的高透光率浅色玻璃 从-550到-492nm。 作为玻璃基体组合物的高透光性浅色玻璃，含有SiO 2：63〜75质量％，Al 2 O 3：0〜5质量％，Na 2 O：5〜15质量％，K 2 O：0〜5质量％ ，CaO：5〜15质量％，MgO：0〜10质量％，作为着色成分，Er2O3：0.3〜3.0质量％，t-Fe2O3：0.05〜0.5质量％，Se：1 至30ppm，氧化还原：超过62％。

    GLASS PRODUCTION PROCESS
    4.
    发明申请
    GLASS PRODUCTION PROCESS 审中-公开
    玻璃生产工艺

    公开(公告)号：US20090000335A1

    公开(公告)日：2009-01-01

    申请号：US12198202

    申请日：2008-08-26

    申请人： Shingo Urata ,  Shuichi Akada ,  Hosaku Yonetsu ,  Hajime Itoh

    发明人： Shingo Urata ,  Shuichi Akada ,  Hosaku Yonetsu ,  Hajime Itoh

    IPC分类号： C03B5/16

    CPC分类号： C03B5/2252 ,  C03C3/087

    摘要： To provide a glass production process capable of reducing bubbles remaining in glass after production, substantially without a refiner.A glass production process, characterized in that glass to be produced is soda lime glass containing water, and the process comprises a step of subjecting molten glass to reduced pressure defoaming in an atmosphere under a pressure of at most the bubble growth starting pressure Peq (kPa) represented by the following formula (1): Peq=−80.8+98.2×[β-OH]+68.0×[SO3]+0.0617×T  (1) wherein [β-OH] is the β-OH value (mm−1) of glass, [SO3] is the content (as represented by mass percentage based on oxides) of SO3 in glass, and T is the temperature (° C.) of the molten glass.

    摘要翻译： 提供一种玻璃制造方法，其能够在生产后能够减少玻璃中残留的气泡，基本上不需要精磨机。 一种玻璃制造方法，其特征在于，所生产的玻璃是含有水的钠钙玻璃，该方法包括在至少气泡生长开始压力Peq（kPa）的压力下，在气氛中使熔融玻璃进行减压脱泡的工序 ）由下式（1）表示：<？in-line-formula description =“In-line Formulas”end =“lead”？> Peq = -80.8 + 98.2x [beta-OH] + 68.0x [SO3] + 0.0617xT（1）<？in-line-formula description =“In-line Formulas”end =“tail”？>其中[β-OH]是玻璃的β-OH值（mm-1），[SO 3 ]是玻璃中SO 3的含量（以氧化物的质量百分数表示），T为熔融玻璃的温度（℃）。

    Light blue flat glass
    5.
    发明授权
    Light blue flat glass 失效
    浅蓝色平板玻璃

    公开(公告)号：US07326665B2

    公开(公告)日：2008-02-05

    申请号：US10653057

    申请日：2003-09-03

    申请人： Shuichi Akada ,  Masato Ooe

    发明人： Shuichi Akada ,  Masato Ooe

    IPC分类号： C03C3/095 ,  C03C3/087

    CPC分类号： C03C4/02 ,  C03C3/095

    摘要： A light blue flat glass which is soda-lime-silica glass and which contains Nd in such an amount that the content based on Nd2O3 represented by mass percentage, is from 0.001 to 0.1%, and no Co or Co in such an amount that the content based on CoO as represented by mass percentage, is less than 0.1 ppm.

    摘要翻译： 一种浅蓝色平板玻璃，其是钠钙石英玻璃，并且其含有以质量百分比表示的基于Nd 2 O 3 3的含量的Nd的量为 0.001〜0.1％，不含以质量百分比表示的以CoO为基准的量的Co或Co小于0.1ppm。