公开(公告)号:US3810793A
公开(公告)日:1974-05-14
申请号:US26466972
申请日:1972-06-20
发明人: HELLER W
CPC分类号: C21D8/08
摘要: A PROCESS FOR MANUFACTURING AN UNANNEALED REINFORCING BAR STEEL FOR PRESTRESSED CONCRETE WHICH COMPRISES SUBJECTING A STEEL HAVING A COMPOSITION OF: 0.20-0.35 WEIGHT PERCENT CARBON 0.20-2.50 WEIGHT PERCENT SILICON 0.50-3.50 WEIGHT PERCENT MANGANESE 1.25-4.50 WEIGHT PERCENT CHROMIUM (MN+CR)=2.75-5.00 WEIGHT PERCENT, THE BALANCE CONSISTING ESSENTIALLY OF IRON BY COOLING IT IN QUIET AIR FROM THE HOT-ROLLED STATE WITH THE FORMATION OF BAINITE STRUCTURE AND, THEREAFTER, EITHER COLD DEFORMING IT PLASTICALLY WITHOUT ESSENTIAL INCREASE OF TENSILE STRENGTH AND TEMPERING THE SAME AT A TEMPERATURE IN THE RANGE OF 100 TO 400* C. OR TEMPERING IT IN THE TEMPERATURE RANGE BETWEEN 150 AND 550* C.