公开(公告)号：US06212928B1

公开(公告)日：2001-04-10

申请号：US09464683

申请日：1999-12-16

申请人： Ki-Ho Kim ,  Gyosung Kim ,  Chang-Hoon Lee ,  Sung-Yul Huh ,  Boeng-Joon Kim

发明人： Ki-Ho Kim ,  Gyosung Kim ,  Chang-Hoon Lee ,  Sung-Yul Huh ,  Boeng-Joon Kim

IPC分类号： B21B2706

CPC分类号： C21D8/1266 ,  B21B3/02 ,  C21D8/0236 ,  C21D8/0268 ,  C21D8/1233

摘要： A method for manufacturing a thin cold rolled inner shield steel sheet for use in a braun tube is disclosed. With this method, a steel sheet with superior magnetic field shielding properties can be manufactured by carrying two steps of cold rolling without adding an expensive alloy element, and without using a special decarburizing facility such as OCA. The method includes the following steps. There is prepared a steel slab composed of, in wt %, 0.0025% or less of C, 0.05-0.25% of Mn, 0.05-0.15% of Si, 0.015 or less of Al, and a balance of Fe and other impurity elements. Then a hot rolling is carried out on the steel slab at a temperature of 910° C. or above. Then a first cold rolling is carried out, and a first annealing is carried out at above a recrystallization temperature. Then a second cold rolling is carried out at a reduction ratio of 25-45%.

摘要翻译： 公开了一种制造用于布朗管中的薄冷轧内屏蔽钢板的方法。 通过这种方法，可以通过在不添加昂贵的合金元素的情况下进行冷轧的两个步骤，并且不使用诸如OCA的特殊脱碳设备来制造具有优异的磁场屏蔽性能的钢板。 该方法包括以下步骤。 制备了以重量％计，C：0.0025％以下，Mn：0.05〜0.25％，Si：0.05〜0.15％，Al：0.015以下，余量由Fe和其他杂质构成的钢坯。 然后在910℃以上的温度下对钢坯进行热轧。 然后进行第一次冷轧，在再结晶温度以上进行第一次退火。 然后以25-45％的压下率进行第二次冷轧。