摘要:
The present invention relates to a polarizer in which contents of zinc, boron, and potassium are controlled to be within a certain range, a polarizing plate, and an image display device having excellent durability and heat resistance, and a method of manufacturing the polarizer. In one embodiment, the present invention provides a polarizer, in which the value of zinc content (wt. %)×boron content (wt. %)/potassium content (wt. %) is 0.1 to 4.0, boron content is 1.0 wt. % to 5.0 wt. % and potassium content is 0.3 wt. % to 2.0 wt. %, based on the weight of the polarizer, a polarizing plate and an image display device including the same. Further, the present invention provides a method of manufacturing a polarizer, the method including at least a dyeing process, a cross-linking process, a stretching process and a washing process.
摘要:
There is provided a method for producing a polarizer having improved cross transmittance. The method for producing a polarizer includes: dyeing a polyvinyl alcohol (PVA)-based film with molecular iodine by immersing the PVA-based film in an aqueous iodine solution (a dyeing step); absorbing the molecular iodine into the PVA-based film using an aqueous boric acid solution (a cross-linking step); arranging the molecular iodine in the certain direction by stretching the PVA-based film in a certain direction (an stretching step); and drying, in an oven, the PVA-based film in which the molecular iodine is oriented; wherein a phosphate compound is added to the iodine aqueous solution (the dyeing step) or the aqueous boric acid solution (the stretching step) so that a weight ratio of the boric acid: the phosphate compound is in a range of 1:0.1 to 1:10.
摘要:
There is provided a method for producing a polarizer having improved cross transmittance. The method for producing a polarizer includes: dyeing a polyvinyl alcohol (PVA)-based film with molecular iodine by immersing the PVA-based film in an aqueous iodine solution (a dyeing step); absorbing the molecular iodine into the PVA-based film using an aqueous boric acid solution (a cross-linking step); arranging the molecular iodine in the certain direction by stretching the PVA-based film in a certain direction (an stretching step); and drying, in an oven, the PVA-based film in which the molecular iodine is oriented; wherein a phosphate compound is added to the iodine aqueous solution (the dyeing step) or the aqueous boric acid solution(the stretching step) so that a weight ratio of the boric acid:the phosphate compound is in a range of 1:0.1 to 1:10.
摘要:
Provided are polarizer, polarizing plate, and image display device having excellent durability and heat resistance in which contents of zinc, boron, and iodine in the polarizer are controlled in a specific range. According to an embodiment of the present invention, a polarizer having a value of zinc content (wt %)×boron content (wt %)/iodine content (wt %) in a range of about 0.1 to about 3.0 in all positions in which a depth (D) from a surface to a center of the polarizer is 0≦D≦200 nm, polarizing plate and image display device including the polarizer are provided. The polarizer, polarizing plate, and image display device according to the present invention have excellent durability and heat resistance in which initial cross transmittance and color are maintained and transmittance, degree of polarization, and color are maintained even under high temperature conditions.
摘要:
Disclosed is an adhesive for a polarizing plate that comprises a polyvinyl alcohol-based resin with an acetoacetyl group and an amine-based metal compound crosslinking agent, and a method of manufacturing the same.
摘要:
Disclosed is an adhesive for a polarizing plate that comprises a polyvinyl alcohol-based resin with an acetacetyl group and an amine-based metal compound crosslinking agent, and a method of manufacturing the same.