摘要:
PAPERS CONTAINING EXPANDED THERMOPLASTIC MICROSPHERES ARE PREPARED BY INCORPORATING AN EXPANDABLE THERMOPLASTIC MICROSPHERE WITHIN THE PULP SLURRY AND THE PAPER DRIED AT ABOUT 90*C., CAUSING THE MICROSPHERES TO FOAM. THIS PHENOMENON APPEARS TO BE PECULIAR TO MICROSPHERES HAVING A VINYLIDENE CHLORIDE-ACRYLONITRILE COPOLYMER SHELL.
摘要:
Cellulosic substrates containing a cationic resinous composition comprising reaction products of (A) adducts of certain dihaloalkanes and alkylene diamine and (B) certain epihalohydrins to increase wet strength.
摘要:
A fibrous sheet having a high strength and water resistance and having no resin specks on the surface can be produced by producing a sheet from a fiber slury by the known paper making process, to said fiber slurry being added a flocculate of chlorinated polymer latices which has a particle size of 100.mu.-500 .mu. and is prepared by heating said chlorinated polymer latices to a temperature of at least their minimum film-forming temperature and then adding a water soluble cationic polymer or a polyvalent metal salt with stirring. Examples of said chlorinated polymer latices are anionic polyvinyl chloride latex, polyvinylidene chloride latex or the combination thereof.
摘要:
The electrostatic recording material comprises an electroconductive transparentized base sheet having a dielectric layer thereon. The transparentized base sheet is obtained by subjecting to a transparentizing treatment with moisture, heat and pressure a fibrous matrix sheet of a mixture of natural pulp with synthetic pulp formed of a blended polymer system consisting essentially of polyvinyl alcohol-acrylonitrile copolymer and acrylonitrile-styrene copolymer.