CN106217825A 制备碳纤维织物增强聚苯硫醚热塑性复合材料的方法 无效 - 驳回

制备碳纤维织物增强聚苯硫醚热塑性复合材料的方法
摘要：
本发明提供一种制备碳纤维织物增强聚苯硫醚热塑性复合材料的方法，包括步骤：将干燥的碳纤维织物浸渍于环氧树脂与丙酮的混合溶液中，其中碳纤维织物为55～61重量份，环氧树脂为1～6重量份，所述环氧树脂与所述丙酮的重量份之比为1∶999～1∶4；5～10min后，将碳纤维织物取出并与29～39重量份的聚苯硫醚薄膜热压成型，制得碳纤维织物预浸料；以及将碳纤维织物预浸料与聚苯硫醚薄膜交替叠放于模具中，制得碳纤维织物增强聚苯硫醚热塑性复合材料。
摘要（英）：

The invention provides a method for preparing polyphenylene sulfide thermoplastic composites reinforced by carbon fiber fabric. The method comprises the following steps: dipping dry carbon fiber fabric in a mixed solution of epoxy resin and acetone, wherein the carbon fiber fabric accounts for 55-61 parts by weight, the epoxy resin accounts for 1-6 parts by weight, and the ratio by weight of the epoxy resin to the acetone is 1:999 to 1:4; after 5-10 minutes, taking out the carbon fiber fabric, and carrying out hot-pressing molding on the carbon fiber fabric and 29-39 parts by weight of polyphenylene sulfide films so as to prepare carbon fiber fabric prepreg; and alternately overlappng the carbon fiber fabric prepreg and the polyphenylene sulfide films in a die so as to prepare the polyphenylene sulfide thermoplastic composites reinforced by the carbon fiber fabric.

0/0