The invention discloses a corrosion resistant and oxidation resistant vanadium-titanium alloy cast iron glass mold material. The corrosion resistant and oxidation resistant vanadium-titanium alloy cast iron glass mold material comprises the following components by mass percent: 3.5 to 3.6% of carbon, 2.0 to 2.15% of silicon, 0.6 to 0.66% of manganese, 0.08% or less of sulfur, 0.08% or less of phosphorus, 0.15 to 0.18% of titanium, 0.075 to 0.09% of vanadium, and 0.75 to 0.9% of molybdenum, and the balance being iron, wherein the mass ratio of titanium to vanadium to molybdenum is 2 to 1 to 10. According to the invention, a glass mold manufactured through the material is applicable to production of high-speed bottle-making machines, is good in corrosion resistance and oxidation resistance, and has excellent heat dissipation performance, and the service life of the glass mold is prolonged.