The present invention is an addition reaction-curable silicone emulsion composition containing a water-soluble silane coupling agent (I) and an organopolysiloxane (II) having at least two alkenyl groups in one molecule thereof, where the water-soluble silane coupling agent (I) has at least one group selected from among a succinic anhydride group, a quaternary ammonium group, and a ureido group, and 1 part by mass or more of the water-soluble silane coupling agent (I) is contained relative to 100 parts by mass of the organopolysiloxane (II). This provides: a silicone emulsion composition that gives a cured film adhering well to plastic film substrates regardless of the type, while having suitable release properties regarding adhesives; and a delamination film made by forming a cured film of the silicone emulsion composition.