A method of manufacturing polyimide particles includes combining a polyimide solution including a polyimide and an organic solvent with an aqueous solution including water in the presence of an emulsifying surfactant at a shear rate from 1,000 to 3,000 revolutions per minute to form an emulsion. The method further includes removing the organic solvent to form an aqueous polymer dispersion including polyimide particles, and recovering the polyimide particles. The polyimide particles have a spherical morphology and a volume based D10 diameter from 3 to 50 micrometers, a volume based D90 diameter from 3 to 80 micrometers, and a volume based D100 diameter from 3 to 100 micrometers.