An object of this invention is to provide a polyimide film suitable for use in flexible printed circuit boards and the like which have high flexibility and dimensional stability, and to provide a laminate and metal-clad laminate which uses such a polyimide film. This invention relates to a multilayer polyimide film being a polyimide film having a multilayer structure, including: a core layer; and clad layers provided on each side of the film, which clad layers are exposed, the core layer being a non-thermoplastic polyimide having an average coefficient of linear expansion at a temperature from 100° C. to 200° C. in a range of 5 ppm/° C. to 20 ppm/° C., each of the clad layers being a polyimide having a peeling strength of 3 N/cm or less, the film as a whole having an average coefficient of linear expansion at a temperature range of 100° C. to 200° C. in a range of 9 ppm/° C. to 30 ppm/° C., and (a)>(b), where (a) is an average modulus of elasticity of the core layer and (b) is an average modulus of elasticity of the clad layers.