Substantially dense, void-free ceramic-metal composites are prepared from components characterized by chemical incompatibility and non-wetting behavior. The composites have a final chemistry similar to the starting chemistry and microstructures characterized by ceramic grains similar in size to the starting powder and the presence of metal phase. A method for producing the composites requires forming a homogeneous mixture of ceramic-metal, heating the mixture to a temperature that approximates but is below the temperature at which the metal begins to flow and presssing the mixture at such pressure that compaction and densification of the mixture occurs and an induced temperature spike occurs that exceeds the flowing temperature of the metal such that the mixture is further compacted and densified. The temperature spike and duration thereof remains below that at which significant reaction between metal and ceramic occurs. The method requires pressure of 60-250 kpsi employed at a rate of 5-250 kpsi/second.