The present invention relates to giant grains or single crystals of chromium. Hitherto, since single crystals of chromium were generally obtained by a floating zone method, it was difficult to obtain an optionally shaped chromium single crystal. The present invention has been made in order to overcome these problems and provides a process for producing single crystals of chromium by secondary recrystallization. That is, it has been found that control of the amount of impurities present in a chromium component such as, for example, Co, Ti, Al, Si, and Ca, has a good influence on the formation of single crystals of chromium. For example, if chromium to which the above-described Ti, Al, Si, and Ca have been added in an amount of from 0.0002 wt % to 0.1 wt %, calculated as oxides thereof, or to which from 0.01 to 3 wt % of Co has further been added, is sintered and the resulting chromium molding is heated treated, single crystals of chromium having a complicated shape can be obtained.