By utilizing the vapor phase polymerization techniques of the present invention, numerous distinct and highly beneficial advantages are realized. For instance, cis-1,4-polyisoprene rubber and high cis-1,4-polybutadiene rubber having a consistent and controllable molecular weight can be easily and practically prepared without utilizing a solvent. The subject invention more specifically discloses a method for vapor phase polymerizing isoprene into cis-1,4-polyisoprene in a process comprising the steps of:(1) charging into a reaction zone said isoprene and a preformed catalyst system which is made by reacting an organoaluminum compound with titanium tetrachloride, preferably in the presence of at least one ether; wherein the isoprene is maintained in the vapor phase in said reaction zone by a suitable combination of temperature and pressure;(2) allowing said isoprene to polymerize into cis-1,4-polyisoprene at a temperature within the range of about 35.degree. C. to about 70.degree. C.; and(3) withdrawing said cis-1,4-polyisoprene from said reaction zone. It has been determined that gel formation can be reduced by conducting the polymerization of isoprene monomer in the presence of a diarylamine, such as para-styrenated diphenylamine.