Disclosed is an aluminum alloy forging for use in automotive suspension parts and the like, and a method of manufacture for same. The aluminum alloy forging contains Si 0.4-1.5 wt %, Fe greater than 0.4 wt % and equal to or less than 1.0 wt %, Cu equal to or less than 0.40 wt %, Mg 0.8-1.3 wt % and Ti 0.01-0.1 wt %; Zn is restricted to equal to or less than 0.05 wt %; and the aluminum alloy forging contains at least one selected from among the following group comprising: Mn 0.01-1.0 wt % and Cr 0.1-0.4%; and Zr 0.05-0.2 wt %. Hydrogen content is restricted to 0.25 ml or less per 100 g of Al, and the remainder is composed of unavoidable impurities and Al. The average grain size is 50 μm or less, the crystallized area ratio is 3% or less, and the average crystallized grain size is 8 μm or less.