The invention relates to an aluminium brazing product, such as a brazing sheet product, comprising an aluminium alloy base substrate (1) of an aluminium alloy comprising silicon in an amount in the range of 2 to 18% by weight, and on at least one outlet surface a layer (2) comprising nickel, wherein a separately deposited layer (3) is applied on one side of said layer (2) comprising nickel, and wherein said layer (3) comprising a metal such that taken together said aluminium base substrate (1) and all layers exterior thereto form a metal filler having a liquidus temperature in the range of 490 to 570 DEG C. The invention also relates to a method of manufacturing such an aluminium brazing product and to a brazed assembly comprising at least one component made of the aluminium brazing product.