    Coating for inhibiting oxidation of a substrate
    2.
    发明公开
    Coating for inhibiting oxidation of a substrate 有权
    Beschichtung zur Oxidationshemmung eines Substrats

    公开(公告)号：EP1382721A1

    公开(公告)日：2004-01-21

    申请号：EP03014489.3

    申请日：2003-07-02

    申请人： The Boeing Company

    发明人： Kendig, Martin W. ,  Hon, Melitta ,  Warren, Leslie

    IPC分类号： C23F11/16 ,  C09D5/08

    CPC分类号： C23F11/161 ,  C09D5/08 ,  C23F11/165 ,  Y10T428/31504

    摘要： A film (11) which may be placed on a metallic substrate (12) to inhibit corrosion of the substrate when in a corrosive environment. The film (11) also inhibits corrosion at a defect area (18) in the film (11) when the substrate (12) is exposed in the presence of a corrosive environment. The film (11) includes dopants (26) which release from the film (11) when corrosion begins at a film defect. Therefore, the film not only inhibits corrosion where the film is undamaged, but also inhibits corrosion at the site of a defect in the film. Advantageously, the system does not lose its effectiveness over a given period of time if no defect occurs in the substrate (Fig. 1).

    摘要翻译： 可以放置在金属基底（12）上以在腐蚀环境中抑制基底腐蚀的薄膜（11）。 当在腐蚀性环境的存在下暴露基板（12）时，膜（11）还抑制膜（11）中的缺陷区域（18）的腐蚀。 膜（11）包括当在膜缺陷处开始腐蚀时从膜（11）释放的掺杂剂（26）。 因此，该膜不仅抑制膜未损伤的腐蚀，而且抑制膜的缺陷部位的腐蚀。 有利地，如果在衬底中没有发生缺陷，系统在给定的时间段内不会失去其有效性（图1）。