公开(公告)号：KR1020110067339A
公开(公告)日：2011-06-22
申请号：KR1020090123900
申请日：2009-12-14
申请人： 한국건설기술연구원
CPC分类号： C04B28/26 , Y02W30/92 , Y02W30/93 , Y02W30/94 , C04B18/08 , C04B18/12 , C04B18/141 , C04B20/026
摘要： PURPOSE: A non-sintering binder, a producing method of a room temperature strength expression concrete composition using thereof, and the concrete composition are provided to secure the excellent compressive strength of the concrete composition at room temperature. CONSTITUTION: A non-sintering binder for the room temperature strength expression contains an alkali activator, and a binder including 5~20wt% of stone powder, 30~50wt% of blast furnace slag, and 30~50wt% of fly ash. The binder and the alkali activator are mixed in a weight ratio of 60~80:40~20. A producing method of a room temperature strength expression concrete composition using the non-sintering binder comprises the following steps: mixing fine aggregate, coarse aggregate, and water; and inserting the non-sintering binder into the mixture.
摘要翻译： 目的：提供非烧结粘合剂，使用其的室温强度表达混凝土组合物的制造方法和混凝土组合物，以确保混凝土组合物在室温下的优异的抗压强度。 构成：用于室温强度表达的非烧结粘合剂含有碱活化剂和包含5〜20wt％石粉，30〜50wt％高炉矿渣和30〜50wt％粉煤灰的粘合剂。 粘合剂和碱活化剂以60〜80：40〜20的重量比混合。 使用非烧结粘合剂的室温强度表达混凝土组合物的制造方法包括以下步骤：混合细骨料，粗骨料和水; 并将非烧结粘合剂插入混合物中。
-
公开(公告)号：KR101042026B1
公开(公告)日：2011-06-16
申请号：KR1020090111915
申请日：2009-11-19
申请人： 한국건설기술연구원
摘要： 본 발명은 보, 바닥판, 거더 및 콘크리트 복공판 등과 같은 프리캐스트 콘크리트로 제작되는 구조체(프리캐스트 구조체)의 제작 단계, 또는 제작 완료 후 현장 설치 단계에서 프리캐스트 구조체의 양중을 편리하게 하기 위하여, 콘크리트 타설 전에 미리 거푸집 등에 설치하여 콘크리트 양생이 끝난 뒤, 걸림장치를 쉽게 걸어서 프리캐스트 구조체를 용이하게 양중할 수 있도록 한 것이다.
본 발명에서는 인양을 위한 샤클(5)이 걸리게 되는 양중고리 장치(1)를 구비한 프리캐스트 콘크리트 구조체로서, 양중고리 장치(1)는, 슬리브 부재(10)와, 고리(12)와, 슬리브 부재(10) 및 고리(12)를 관통하며 양단부가 슬리브 부재(10)의 외부로 돌출되는 지지봉(11)을 포함하며; 슬리브 부재(10)가 수직하게 놓인 상태에서 콘크리트가 타설되어 지지봉(11)의 외부 돌출 단부와 슬리브 부재(10)의 외면이 콘크리트에 매립되어 있는 상태로 양중고리 장치(1)가 콘크리트에 일체로 구비되고; 고리(12)는 슬리브 부재(10) 내에 위치하고 있다가, 인양시에는 고리(12)의 상단부가 슬리브 부재(10) 외부로 노출되어 샤클(5)이 고리(12)에 걸리고, 고리(12)의 하부가 지지봉(11)에 걸리게 되어 프리캐스트 콘크리트 구조체가 인양되는 양중고리 장치를 구비한 프리캐스트 콘크리트 구조체와, 이러한 양중고리 장치가 제공된다.-
公开(公告)号：KR1020110051914A
公开(公告)日：2011-05-18
申请号：KR1020090108733
申请日：2009-11-11
申请人： 한국건설기술연구원
摘要： PURPOSE: A method for manufacturing a steel-fiber-reinforced cement composite is provided to improve the ductile behavior and the mechanical adhesive of the composite based on wave type steel fiber and straight type steel fiber. CONSTITUTION: Mortar is obtained by mixing sand, reactive powder, a filling material, thickening agent with the cement. The mortar is mixed with mixing water in which 90 to 99.5 weight% of water and 0.5 to 10 weight% of a water reducing agent. 1 to 5vol% of straight type steel fiber and wave type steel fiber are added, based on 100vol% of the concrete. The mortar mixture is cured for 1 to 3 days under a wet condition and is cured for 2 to 4 days under a vapor condition.
摘要翻译： 目的：提供一种钢纤维增强水泥复合材料的制造方法，以提高基于波浪型钢纤维和直型钢纤维的复合材料的延展性能和机械粘合剂。 构成：砂浆通过将砂，活性粉末，填充材料，增稠剂与水泥混合而获得。 将砂浆与混合水混合，其中90-99.5重量％的水和0.5-10重量％的减水剂。 基于100vol％的混凝土，添加1〜5vol％的直型钢纤维和波浪型钢纤维。 砂浆混合物在潮湿条件下固化1至3天，并在蒸气条件下固化2至4天。
-
公开(公告)号：KR101018008B1
公开(公告)日：2011-03-02
申请号：KR1020080082209
申请日：2008-08-22
CPC分类号： C04B28/006 , C04B2111/1037 , C04B2201/50 , C04B2201/52 , Y02P40/165 , Y02W30/92 , Y02W30/94 , C04B12/04 , C04B14/02 , C04B18/08 , C04B18/141 , C04B20/0076 , C04B20/0096 , C04B22/062 , C04B2103/302 , C04B14/185 , C04B2103/10
摘要： 본 발명은 플라이애쉬와 고로슬래그를 이용한 무시멘트 콘크리트의 제조방법에 관한 것으로, 그 목적하는 바는 제조 시 이산화탄소를 다량으로 배출하는 시멘트 대신에 결합재로서 적정비율의 플라이애쉬와 고로슬래그를 동시에 적용하고, 또한 활성화제로서 적정비율의 NaOH와 쇼듐실리케이트를 적용하여, 작업성이 우수하고 상온양생 가능한 압축강도 80MPa급의 무시멘트 콘크리트의 제조방법을 제공하고자 하는데 있다.
상기 목적을 달성하기 위한 본 발명은 배합원료로서 결합재, 활성화제, 잔골재, 굵은골재, 물 및 고성능감수제를 포함하고, 이들 배합원료를 배합하고, 교반하는 과정과 양생하는 과정을 거쳐 콘크리트를 제조하는 방법에 있어서, 상기 결합재는 분말도 2,000~4,000cm
2 /g의 플라이애쉬와 3,000~5,000cm
2 /g의 고로슬래그가 중량비로 1:1의 비율로 구성되는 것이며, 상기 활성화제는 6~12Mole NaOH와 쇼듐실리케이트가 중량비로 0.75:1.25~1.25:0.75의 비율로 구성되는 것임을 특징으로 한다.
플라이애쉬, 고로슬래그, 무시멘트 콘크리트, 시멘트 ZERO 콘크리트, NaOH-
公开(公告)号：KR1020100069881A
公开(公告)日：2010-06-25
申请号：KR1020080128427
申请日：2008-12-17
申请人： 한국건설기술연구원
摘要： PURPOSE: A manufacturing method of a steel fiber for an ultra high performance fiber reinforced concrete and a concrete using the same are provided to increase the mechanical performance such as compressive strength and flexural strength. CONSTITUTION: A steel fiber for an ultra high performance fiber reinforced concrete is mixed in a cement complex and improves the tensile strength of the composite. The steel fiber is formed with a wave shape. The wave number of the steel fiber is 4~8. The wave depth of the steel fiber is 0.12~0.35mm. The wave length of the steel fiber is 1.86~3.82mm. The diameter of the steel fiber is 0.15~0.35mm. The length of the steel fiber is 10~30mm. The tensile strength of the steel fiber is 2000~4000MPa.
摘要翻译： 目的：提供一种用于超高性能纤维增强混凝土的钢纤维的制造方法和使用其的混凝土，以增加抗压强度和抗弯强度等机械性能。 构成：将超高性能纤维增强混凝土用钢纤维混合在水泥复合体中，提高复合材料的拉伸强度。 钢纤维形成波形。 钢纤维的波数为4〜8。 钢纤维波浪深度为0.12〜0.35mm。 钢纤维的波长为1.86〜3.82mm。 钢纤维的直径为0.15〜0.35mm。 钢纤维的长度为10〜30mm。 钢纤维的拉伸强度为2000〜4000MPa。
-
公开(公告)号：KR1020100037889A
公开(公告)日：2010-04-12
申请号：KR1020080097224
申请日：2008-10-02
申请人： 한국건설기술연구원
CPC分类号： Y02W30/91 , Y02W30/92 , C04B28/006 , C04B40/02 , C04B2103/302 , C04B2201/52
摘要： PURPOSE: A method for manufacturing cement-free concrete using waste glass micropowder and fly ash is provided to secure compressive strength to 20~60MPa range, to obtain excellent workability by maintaining mobility for one hour, and to reduce the generation of CO2 gas in manufacturing the cement. CONSTITUTION: A method for manufacturing cement-free concrete comprises the following steps: mixing a binder, an activator, fine aggregates, thick aggregates, water, and water reducing agent; and the manufacturing the concrete by curing the mixture. The binder comprises waste glass micropowder of 2,000~4,000cm^2 / g and fly ash of 2,000~5,000cm^2 / g in a weight ratio of 3:97~20:80, respectively. The activator includes NaOH of 6~12 mole and sodium silicate in the weight ratio of 0.75:1.25~1.25:0.75, respectively.
摘要翻译： 目的：提供使用废玻璃微粉和飞灰制造无水泥混凝土的方法，以将压缩强度保持在20〜60MPa的范围内，通过保持流动性1小时获得优异的可加工性，并减少制造中的二氧化碳气体的产生 水泥。 构成：制造无水泥混凝土的方法包括以下步骤：混合粘合剂，活化剂，细骨料，浓骨料，水和减水剂; 并通过固化混合物制造混凝土。 粘合剂包括2,000〜4000cm ^ 2 / g的废玻璃微粉，重量比为3：97〜20：80的粉煤灰为2,000〜5,000cm ^ 2 / g。 活化剂包括6〜12摩尔的NaOH和重量比为0.75：1.25〜1.25：0.75的硅酸钠。
-
公开(公告)号：KR100819168B1
公开(公告)日：2008-04-04
申请号：KR1020060100206
申请日：2006-10-16
申请人： 한국건설기술연구원
摘要： An optimal design method of a structure is provided to offer the optimum design criteria by using physical properties of UHPCC(ultra-high performance cementitious composites) to the maximum when manufacturing a single-span girder with UHPCC(ultra-high performance cementitious composites). An optimal design method of a structure is provided for making the optimum design for an RC or PSC I-type girder possible using UHPCC(ultra-high performance cementitious composites), wherein the UHPCC(ultra-high performance cementitious composites) are manufactured by inputting mixing water composed of water and high-performance water reducing agents into premixing type mortar composed of cement, sand, reactive powder, filler and thickener and mixing with a high-speed mixer, inputting steel fibers having different sizes into an admixture of the mortar and the mixing water in the single or hybrid type and re-mixing, and then curing for the appointed period.
摘要翻译： 提供了一种最佳的结构设计方法，通过在使用UHPCC（超高性能水泥复合材料）制造单跨梁时，通过使用UHPCC（超高性能水泥复合材料）的物理性能达到最大值，从而提供最佳设计标准。 提供了一种结构的最优设计方法，可以使用UHPCC（超高性能水泥复合材料）制作RC或PSC I型梁的最佳设计，其中UHPCC（超高性能水泥复合材料）是通过输入 将由水和高性能减水剂组成的水混合到由水泥，砂，活性粉末，填料和增稠剂组成的预混合砂浆中，并与高速混合机混合，将不同尺寸的钢纤维输入到砂浆和 混合水在单一或混合型中再次混合，然后在指定时间内固化。
-
公开(公告)号：KR1020050100513A
公开(公告)日：2005-10-19
申请号：KR1020040025783
申请日：2004-04-14
申请人： 한국건설기술연구원
IPC分类号： B28C5/40
CPC分类号： B28C5/0831 , B28C5/40 , B28C7/026 , B28C7/14
摘要： 본 발명은 시멘트 복합체를 혼합하기 위한 믹서에 관한 것으로서, 특히 시멘트 복합체의 혼합 조건 중 가장 중요한 요소인 믹서 내의 스페이드(spade)의 속도를 높게 유지하면서도 혼합 시에 스페이드에 걸리는 큰 부하를 극복할 수 있고, 시멘트 복합체의 인성 확보를 위해 사용되는 섬유를 자동으로 믹서 내로 투입할 있는, 시멘트 복합체를 혼합하기 위한 믹서에 관한 것이다. 본 발명에 따른 시멘트 복합체를 혼합하기 위한 믹서는 서로 연결되는 상판과 하판으로 구성된 프레임과, 프레임의 하판에 고정되고 혼합을 위해 시멘트 복합체가 투입되는 투입구와 혼합이 종료된 후 혼합된 시멘트 복합체를 배출시키기 위한 배출구를 갖는 드럼과, 시멘트 복합체를 혼합하기 위해 드럼 상부에 결합되는 회전 수단과, 회전 수단에 동력을 제공하는 구동 수단 및 회전 수단에 의해 혼합되는 시멘트 복합체에 섬유를 투입하기 위한 섬유 공급 수단으로 구성된다.
-
公开(公告)号：KR100502243B1
公开(公告)日：2005-07-20
申请号：KR1020030013180
申请日：2003-03-03
申请人： 한국건설기술연구원
IPC分类号： C04B22/10
CPC分类号： C04B28/02 , C04B40/0039 , C04B41/009 , C04B41/5089 , C04B2103/14 , C04B2103/445 , C04B2103/61 , C04B2111/26 , C04B22/0013 , C04B22/10 , C04B22/124 , C04B41/46 , C04B2103/40 , C04B41/5016
摘要： 본 발명은 콘크리트 무기경화 첨가제로 사용되는 조성물 및 콘크리트 표면 처리 방법에 관한 것으로, 특히, 산업폐기물을 재활용하기 위한 시멘트 고형화를 함에 있어서 유해원소의 용출량을 현저히 줄이고, 콘크리트 내부 강도를 증가시킬 수 있도록 하는 콘크리트 무기경화 첨가제용 조성물 및 표면 처리 방법에 관한 것이다. 본 발명에 따른 콘트리트 무기경화 첨가제용 조성물은 탄산나트륨 5 내지 15 중량%; 염화칼륨 2 내지 8 중량%; 염화암모늄 2 내지 6 중량%; 보락스 0.1 내지 4 중량%; 및 증류수 90.9 내지 77 중량%으로 이루어져 있으며, 본 발명에 따른 콘크리트 처리 방법은 고형화된 콘크리트 구조물의 표면 위에, 규산나트륨(Na
2 O·3SiO
2 ) 40~60중량%, 실리콘 또는 불소 성분이 함유된 계면활성제 0.05~1.0 중량% 및 증류수 39.0~59.95 중량%로 이루어진 조성물을 균일하게 도포하는 단계; 및 상기 조성물이 도포된 표면에 질산, 황산 또는 구연산을 균일하게 도포하는 단계를 포함한다.-
60.发明公开염해 및 중성화를 받아 성능이 저하된 철근콘크리트구조물의 표면처리형 성능 개선제용 조성물 및 그의제조방법 失效性能改善剂的表面处理由盐损伤和中和引起的钢铁混凝土结构的表面处理及其制备的组成
公开(公告)号：KR1020030065099A
公开(公告)日：2003-08-06
申请号：KR1020020005551
申请日：2002-01-31
申请人： 한국건설기술연구원
IPC分类号： C04B28/26
CPC分类号： C04B28/26 , C04B26/04 , C04B2111/00482 , C04B2111/72 , E04G23/02
摘要： PURPOSE: A composition of performance-improving agent for surface treatment of deteriorated steel-concrete structure is provided to fix chloride ions in the concrete structure, protect the corrosion of steel and improve pH of deteriorated concrete by coating concrete structure with a surface treatment agent several times. CONSTITUTION: The surface treatment agent comprises the components of; 15-70wt.% of sodium silicate such as Na2O3SiO2 or Na2O4SiO2; 0.05-5.0wt.% of biochemical material as a catalyst, such as sodium alginate(C6H7NaO6) or casein to improve durability and waterproofness; 25-84.05wt.% of distilled water; and optionally less than 3.0wt.% of surfactant such as C5H8SO2LiF(C2F4)3-8 or (C2H4O)nHF(C2F4)3-8, to lower viscosity of the mixture, less than 7.0wt.% of steel corrosion inhibitor such as triethanol amine, and alkali such as NaOH or Ca(OH)2 to maintain the pH of the mixture between 13-14. The surface treatment agent is prepared by mixing the above materials, heating to 70-100deg.C for 1-2hrs, and applying 5-50drops of acetic acid in a rate of one drop per 1-5hrs for homogeneous mixing.
摘要翻译： 目的：提供一种用于钢筋混凝土结构劣化的表面处理性能改进剂组合物，用于固定混凝土结构中的氯离子，通过用表面处理剂涂覆混凝土结构，保护钢的腐蚀和改善劣化混凝土的pH值 倍。 构成：表面处理剂包括： 15-70重量％的硅酸钠如Na 2 O 3 SiO 2或Na 2 O 4 SiO 2; 0.05-5.0重量％的生化材料作为催化剂，如藻酸钠（C6H7NaO6）或酪蛋白，提高耐久性和防水性; 25-84.05重量％的蒸馏水; 和任选地小于3.0重量％的表面活性剂如C 5 H 8 SO 2 LiF（C 2 F 4）3-8或（C 2 H 4 O）n HF（C 2 F 4）3-8，以降低混合物的粘度，小于7.0重量％的钢腐蚀抑制剂如 三乙醇胺和碱如NaOH或Ca（OH）2以保持混合物的pH在13-14之间。 表面处理剂通过将上述物质混合，加热至70-100℃，持续1-2小时，并以1-5分钟的速率加入5-50滴乙酸，进行均匀混合。
-
-
-
-
-
-
-
-
-