摘要:
In a toner kit having i) a non-magnetic black toner having at least carbon black and ii) color toners, the black toner has a weight-average particle diameter represented by D4b and a one-point method BET specific surface area represented by Sb, and the color toners, other than the-black toner, each have a weight-average particle diameter represented by D4c and a one-point method BET specific surface area represented by Sc, where the black toner and color toners satisfy the following relations (1) and (2): 0.60≦D4.c/D4b≦0.96,: Relation (1) 0.750≦Sc/Sb≦1.000;: Relation (2) and each have an average circularity of from 0.950 to 1.000 and a circularity standard deviation of less than 0.040 as measured with a flow type particle image analyzer.
摘要:
The present invention provides a silica fine particle capable of preventing a charging member or an image bearing member from being contaminated with toner when the toner contains the particle and also capable of providing the toner with a stable developing property. The silica fine particle of the present invention has been hydrophobic treated. Furthermore, the particle has a peak in a range of 0.04 μm to 1 μm and a peak in the range of 1 μm to 100 μm in a volume-basis particle diameter distribution. The particle has a frequency ratio of 10 to 80% for the particles with a particle diameter of 0.04 μm to 1 μm to a total of all the peaks, and the particles has the frequency ratio of less than 16% for the particles with a particle diameters of 20 μm to 2000 μm to the total of all the peaks.
摘要:
In a toner kit having i) a non-magnetic black toner having at least carbon black and ii) color toners, the black toner has a weight-average particle diameter represented by D4b and a one-point method BET specific surface area represented by Sb, and the color toners, other than the-black toner, each have a weight-average particle diameter represented by D4c and a one-point method BET specific surface area represented by Sc, where the black toner and color toners satisfy the following relations (1) and (2): 0.60≦D4.c/D4b≦0.96, Relation (1): 0.750≦Sc/Sb≦1.000; Relation (2): and each have an average circularity of from 0.950 to 1.000 and a circularity standard deviation of less than 0.040 as measured with a flow type particle image analyzer.
摘要:
In a toner kit having i) a non-magnetic black toner having at least carbon black and ii) color toners, the black toner has a weight-average particle diameter represented by D4b and a one-point method BET specific surface area represented by Sb, and the color toners, other than the black toner, each have a weight-average particle diameter represented by D4c and a one-point method BET specific surface area represented by Sc, where the black toner and color toners satisfy the following relations (1) and (2): 0.60≦D4c/D4b≦0.96, Relation (1) 0.750≦Sc/Sb≦1.000; Relation (2) and each have an average circularity of from 0.950 to 1.000 and a circularity standard deviation of less than 0.040 as measured with a flow type particle image analyzer.
摘要:
To provide an method for forming an image capable of effectively suppressing a toner from deteriorating and also capable of keeping the quality of an image for a long period of time, even when the method is applied to an apparatus with as high process speed. The prevent invention provides an method for forming an image, in which a developing unit is used, which includes: a rotatable cylindrical toner bearing member having a diameter represented as Rd (mm); and a rotatable cylindrical toner-supplying member having a diameter Rs (mm), the diameters Rd and Rs satisfying the following relational expression (1): 1≦Rs−Rd≦10 (1) and in which the nonmagnetic one-component toner having an degree of aggregation of 5 to 30% and an electric resistivity of 1×1014 to 1×1018 Ω·cm at an electric field of 1×104 V/cm is used.
摘要:
In a full-color image-forming method having at least a charging step, a latent-image-forming step, a developing step of developing an electrostatic latent image by the use of a developer; a transfer step, and a fixing step, the developer comprises a plurality of color developers and a black developer. The color developers are each a two-component developer for full-color image formation which has i) a color toner having color toner particles containing at least a binder resin, a colorant and a wax and ii) a carrier for the color developer. The black developer is a two-component developer for full-color image formation which has i) a black toner having black toner particles containing at least a binder resin, carbon black and a wax and ii) a carrier for the black developer. The carrier for the black developer has a larger absolute value of charge quantity when the same toner is used, than the respective carriers for the color developers.
摘要:
A toner is provided which has toner particles and a fine silica powder mixed by external addition to the toner particles. The toner has a weight average particle diameter of 4.0 to 9.0 μm. The fine silica powder is subjected to hydrophobic treatment with dimethylsilicone oil, and has, in particle size distribution based on volume, a peak at which cumulative frequency is largest, in the measurement range of 0.02 μm to 1,000.00 μm; the cumulative frequency of 0.10 μm to less than 1.00 μm being 7.0% or less, and, the fine silica powder fulfills the following conditions: 1) A+B≧93.0; 2) 0.45≦A/B≦6.00; and 3) the value of [(carbon content of the treated fine silica powder)/(BET specific surface area of fine silica powder before hydrophobic treatment)] is 0.030 or more to 0.055 or less.
摘要:
A toner is provided which has toner particles and a fine silica powder mixed by external addition to the toner particles. The toner has a weight average particle diameter of 4.0 to 9.0 μm. The fine silica powder is subjected to hydrophobic treatment with dimethylsilicone oil, and has, in particle size distribution based on volume, a peak at which cumulative frequency is largest, in the measurement range of 0.02 μm to 1,000.00 μm; the cumulative frequency of 0.10 μm to less than 1.00 μm being 7.0% or less, and, the fine silica powder fulfills the following conditions: 1) A+B≧93.0; 2) 0.45≦A/B≦6.00; and 3) the value of [(carbon content of the treated fine silica powder)/(BET specific surface area of fine silica powder before hydrophobic treatment)] is 0.030 or more to 0.055 or less.
摘要翻译:提供了一种调色剂,其具有通过外部添加到调色剂颗粒而混合的调色剂颗粒和二氧化硅微粉。 调色剂的重均粒径为4.0〜9.0μm。 用二甲基硅油对二氧化硅微粉进行疏水处理,在0.02μm〜1,000.00μm的测定范围内,以体积分布为基准的粒径分布为累积频率最大的峰值。 0.10μm至小于1.00μm的累积频率为7.0%以下,二氧化硅微粉满足以下条件:1)A + B> = 93.0; 2)0.45 <= A / B <= 6.00; 3)[(二氧化硅微粉处理的碳含量)/(疏水处理前的二氧化硅微粉末的BET比表面积)]为0.030以上至0.055以下。
摘要:
A toner having a good chargeability stable against an environmental change is formed of toner particles each comprising at least a binder resin, a colorant, a release agent and a sulfur-containing polymer, and an external additive. The toner particles contain 100 to 30,000 ppm by weight thereof of at least one stabilizer element selected from the group consisting of magnesium, calcium, barium, zinc, aluminum and phosphorus. The toner particles may preferably be produced by suspension polymerization of a monomer composition containing the sulfur-containing polymer in an aqueous medium containing a dispersion stabilizer having the stabilizer element.
摘要:
A process for producing a polymerization toner, which comprises preparing a polymerizable-monomer composition which contains at least a polymerizable monomer and a colorant and does not contain any polymerization initiator, i) introducing the polymerizable-monomer composition into an aqueous medium to effect granulation, adding a polymerization initiator to the aqueous medium in the course of the granulation or after the granulation has been completed, or ii) adding a polymerization initiator in an aqueous medium, introducing the polymerizable-monomer composition into the aqueous medium to effect granulation, and then polymerizing the polymerizable-monomer composition having been granulated, to produce toner particles. In the process, the polymerization initiator is added in a specific time and a specific manner.