摘要:
A solid polymeric substrate having a resin derived from curable silylated polyurethane composition exhibiting superior properties adhered thereto. The silylated polyurethane is prepared by reacting a polyol component with a diisocyanate component to form a hydroxyl-terminated prepolymer and endcapping the prepolymer with an isocyanate silane.
摘要:
Disclosed herein is a process for preparing a shelf-stable, one-pack, silane modified (meth)acrylic latex interpolymer composition, wherein the process comprises continuously adding at least a portion of a mixture comprising at least 0.5 mole percent of a vinyl silane comprising hydrolyzable groups and up to 99.5 mole percent of a (meth)acrylic monomer to water and a surfactant in a reaction vessel, wherein said addition is carried out in the presence of a polymerization initiator and buffer sufficient to maintain the pH of the reaction at a level of at least 6 throughout the reaction, while simultaneously hydrolyzing from about 10 to about 60% of the hydrolyzable groups of the vinyl silane.
摘要:
In accordance with the present invention, a hydrolyzable silane of low VOC-generating potential is provided which possesses: (i) at least one organofunctional group, said group being a non-bulky electron-withdrawing group and/or a group which interacts with an organic resin, the organofunctional group being bonded to a silicon atom of a hydrolyzable silyl group through a stable bridging groups; and (ii) at least one hydrolyzable group bonded to silicon and containing at least two heteroatoms selected from the group consisting of oxygen, nitrogen and their combinations, hydrolysis of the hydrolyzable group generating a compound having a vapor pressure lower than 0.1 mm Hg at 20° C. Further in accordance with the invention, a resinous composition of low VOC-generating potential is provided which comprises: a) a resinous composition property-enhancing amount of at least one hydrolyzable silane of low VOC-generating potential which possesses: (i) at least one organofunctional group, said group being a non-bulky electron-withdrawing group and/or a group which interacts with an organic resin (b), the organofunctional group being bonded to a silicon atom of a hydrolyzable silyl group through a stable bridging group, and (ii) at least one hydrolyzable group bonded to silicon and containing at least two heteroatoms selected from the group consisting of oxygen, nitrogen and their combinations, hydrolysis of the hydrolyzable group generating a compound having a vapor pressure lower than 0.1 mm Hg at 20° C; and, b) at least one organic resin containing at least one group capable of reacting with organofunctional group (i) of hydrolyzable silane (a) and/or with water.
摘要:
A crosslinkable silane-terminated polymer is provided which includes the reaction product of an isocyanate-terminated prepolymer and a silane possessing a plurality of hydrolysable sites and at least one active hydrogen-containing group which is reactive for isocyanate, the silane upon hydrolysis produces a reduced amount of volatile organic compound compared to that produced by the hydrolysis of a silane possessing an equivalent number of hydrolyzable sites all of which are hydrolyzable alkoxy groups.
摘要:
Powder coating formulations which include as a component thereof a silyl carbamate of the formula: where R1 is a hydrocarbon or acyl group; R2 is a monovalent hydrocarbon group; R3 is alkylene, optionally interrupted with one or more ether oxygen atoms; a is 0 or 1; X is an m-valent organic group; m is 1-6; and, either A=NH and B=O, or A=O and B=NH. The silanes are useful as crosslinkers and/or adhesion promoters.