摘要:
To provide the thermosetting powder coating composition which comprises a fluorine-containing copolymer having crosslinkable functional group and a curing agent, in which the fluorine-containing copolymer has a fluoroolefin unit, has a fluorine content of not less than 10% by weight and is not dissolved in tetrahydrofuran substantially. A coating line can be shared with other powder coating composition because even when the composition mixes to other powder coating composition, it causes no coating defects, and yet a coated article having a coating film excellent in physical properties can be provided.
摘要:
Disclosed are a gas separating membrane prepared from a polymer from a monomer represented by the formula (1): ##STR1## wherein X is chlorine atom or fluorine atom, Y is hydrogen atom or methyl group, and m is 0 or an integer of 1 to 5, and a gas separating membrane prepared from a polymer of the monomer of the formula (1) in an amount of up to 100% by weight and other ethylenically unsaturated monomer in an amount of not more than 50% by weight, based on the combined weight of the monomer of the formula (1) and the other ethylenically unsaturated monomer.
摘要:
This invention provides a process for preparing an .alpha.-fluoroacrylic acid ester characterized by reacting 2,2,3,3-tetrafluorooxetane, a metal halide, an alcohol and a dehalogenating agent. This invention also provides a process for preparing .alpha.-fluoroacrylic acid fluoride, CH.sub.2 .dbd.CFCOF, which is an intermediate for preparing the .alpha.-fluoroacrylic acid ester.
摘要:
A copolymer for optical fibers of fluoroalkylmethacrylate and methacrylic acid, the fluoroalkylmethacrylate having such properties that a homopolymer made of only the fluoroalkylmethacrylate has a glass transition temperature and a refractive index each in the range given by the following formulae (I) and (II), respectively:(1/Tg).ltoreq.9.47.times.10.sup.-3 -4.556.times.10.sup.-3 n.sup.20 (I)n.sup.20 .ltoreq.1.42 (II)wherein Tg represents the glass transition temperature (.degree.K.) of the homopolymer and n.sup.20 represents the refractive index thereof.