公开(公告)号：US4769351A

公开(公告)日：1988-09-06

申请号：US45564

申请日：1987-05-04

申请人： Shigeyuki Soumiya ,  Masahiro Yoshimura ,  Zenjiro Nakai ,  Kazumitsu Hishinuma ,  Takao Kumaki

发明人： Shigeyuki Soumiya ,  Masahiro Yoshimura ,  Zenjiro Nakai ,  Kazumitsu Hishinuma ,  Takao Kumaki

IPC分类号： C01F7/34 ,  C01G25/00 ,  C04B35/119 ,  C04B35/486 ,  C04B35/488 ,  C04B35/626 ,  C04B35/10 ,  C04B35/48

CPC分类号： C04B35/62605 ,  B82Y30/00 ,  C01F7/34 ,  C01G25/00 ,  C04B35/119 ,  C04B35/486 ,  C04B35/4885 ,  C04B35/626 ,  C01P2002/72 ,  C01P2002/88 ,  C01P2004/64 ,  C04B2235/02 ,  C04B2235/3218 ,  C04B2235/322 ,  C04B2235/444 ,  C04B2235/762 ,  C04B2235/765 ,  C04B2235/77 ,  C04B2235/96 ,  Y10S977/775 ,  Y10S977/776 ,  Y10S977/835 ,  Y10S977/896 ,  Y10S977/90

摘要： A process for preparing a zirconia-alumina base composite ultra-fine powder is described, including the steps of: mixing an aluminum salt or an alumina hydrate with an aqueous zirconium oxychloride solution, with or without metal salt acting as a stabilizer; mixing urea or a substance capable of generating ammonia by hydrolysis with the resulting mixture; and allowing the mixture to react at a temperature of 140.degree. to 300.degree. C. and a pressure of 4 to 150 kg/cm.sup.2 in a high-temperature and -pressure vessel. The reaction product is further dried, calcined and crushed to obtain an ultra-fine powder.

摘要翻译： 描述了制备氧化锆 - 氧化铝基复合超细粉末的方法，包括以下步骤：将铝盐或氧化铝水合物与氯氧化锆水溶液混合，用或不用作为稳定剂的金属盐; 混合尿素或能够通过水解产生氨的物质与所得混合物混合; 并在高温压力容器中使混合物在140℃至300℃的温度和4至150kg / cm2的压力下反应。 将反应产物进一步干燥，煅烧和粉碎以获得超细粉末。