摘要:
A poly(urea-ureathane) based on polydimethyl siloxane is prepared by reacting an amino-terminated polydimethyl siloxane with polyisocyanate to form a prepolymer of poly(urea-urethane), and reacting the prepolymer and a chain extender in the presence of a catalyst. The resulting poly(urea-urethane) contains about 5-65 wt % of hard segments, and has a surface resistance of about 10-150 MΩ at high relative humidity, so that it can be used in anti-static electricity and electrostatic discharge shielding.
摘要:
The method of the present invention includes grafting a glycidyl alkylene trialkoxy silane to a novolac phenolic resin in an organic solvent to form a modified novolac phenolic resin; mixing a tetralkoxy silane, an acid and water with the resulting organic solution containing the modified novolac phenolic resin, wherein hydrolysis and condensation reactions are carried out to form a —Si—O—Si— bonding; adding a curing agent for novolac phenolic resin to the resulting reaction mixture; evaporating the organic solvent and acid from the resulting mixture and heating the resulting mixture to form a novolac phenolic resin/silica hybrid organic-inorganic nanocomposite.
摘要:
A polysiloxane-urethane macromonomer having an unsaturated bond on one end thereof was co-polymerized with acrylic acid or acrylate monomers to form a copolymer having polysiloxane-urethane groups as a side chain thereof.
摘要:
The invention provides a technique for improving the flexibility of a cured epoxy resin. An isocyanate terminated polydimethylsiloxane urethane as a modifier is grafted to an epoxy resin. The modified epoxy resin after being cured exhibits an improved flexibility.
摘要:
The method of the present invention includes grafting a glycidyl alkylene trialkoxy silane to a novolac phenolic resin in an organic solvent to form a modified novolac phenolic resin; mixing a tetralkoxy silane, an acid and water with the resulting organic solution containing the modified novolac phenolic resin, wherein hydrolysis and condensation reactions are carried out to form a —Si—O—Si— bonding; adding a curing agent for novolac phenolic resin to the resulting reaction mixture; evaporating the organic solvent and acid from the resulting mixture and heating the resulting mixture to form a novolac phenolic resin/silica hybrid organic-inorganic nanocomposite.
摘要:
In the present invention, vinylimidazole and [3-(methacryloxy)propyl]trimethoxysilane are copolymerized to form a modified polyvinylimidazole, which then undergoes hydrolysis and condensation reactions with water and tetramethoxysilane to prepare a hybrid of polyvinylimidazole and silica. Experimental analyses show that covalent bondings exist between the modified polyvinylimidazole and silica in the hybrid.