摘要:
A non-reducing dielectric ceramic contains Ca, Zr and Ti as metallic elements and does not contain Pb. In a CuK&agr; X-ray diffraction pattern, the ratio of the maximum peak intensity of secondary crystal phases to the maximum peak intensity at 2&thgr;=25° to 35° of a perovskite primary crystal phase is about 12% or less, the secondary crystal phases including all the crystal phases other than the perovskite primary crystal phase. The non-reducing dielectric ceramic exhibits superior insulating resistance and dielectric loss after firing in a neutral or reducing atmosphere and high reliability in a high-temperature loading lifetime test and is useful for producing compact high-capacitance monolithic ceramic capacitors.
摘要:
A non-reducing dielectric ceramic contains Ca, Zr and Ti as metallic elements and does not contain Pb. In a CuK&agr; X-ray diffraction pattern, the ratio of the maximum peak intensity of secondary crystal phases to the maximum peak intensity at 2&thgr;=25° to 35° of a perovskite primary crystal phase is about 12% or less, the secondary crystal phases including all the crystal phases other than the perovskite primary crystal phase. The non-reducing dielectric ceramic exhibits superior insulating resistance and dielectric loss after firing in a neutral or reducing atmosphere and high reliability in a high-temperature loading lifetime test and is useful for producing compact high-capacitance monolithic ceramic capacitors.
摘要:
A nonreducing dielectric contains a main-component having a perovskite crystal phase and satisfying the formula (Ca1-a-b-cSraBabMgc)m(Zr1-w-x-y-zTiwMnxNiyHfz)O3 and a compound oxide represented by the formulae (Si, T)O2—MO—XO and (Si, T)O2—(Mn, M′)O—Al2O3. The ratio of the intensity of the maximum peak of a crystal phase not of the perovskite crystal phase to the intensity of the maximum peak assigned to the perovskite crystal phase appearing at 2&thgr;=25 to 35° is about 5% or less in a CuK&agr; X-ray diffraction pattern.
摘要:
An anti-reducing dielectric ceramic composition having a dielectric constant of 100 or higher and excellent reliability during a life measuring test under a high temperature load and a monolithic ceramic capacitor formed by using the improved anti-reducing dielectric ceramic composition. The composition is a composite oxide represented by the composition formula (Ca1−xSrx)m(Zr1−yTiy)O3, 0≦x
摘要翻译:介电常数为100以上的抗还原性电介质陶瓷组合物,在高温负载下的寿命测定试验中具有优异的可靠性以及使用改进的抗还原性电介质陶瓷组合物形成的叠层陶瓷电容器。 该组合物是以组成式(Ca1-xSrx)m(Zr1-yTiy)O3,0 <= x <0.5,0.60