公开(公告)号:US20170072458A1
公开(公告)日:2017-03-16
申请号:US15125491
申请日:2015-03-23
发明人: Akira YOSHIKAWA , Yuui YOKOTA , Muneki NAKAMURA , Kunihiro TANAKA , Tatsuya NAKAZAWA , Koichi SAKAIRI
CPC分类号: B22D11/005 , B22D11/00 , B22D11/001 , B22D11/11 , B22D21/005 , C22C1/02 , C22C5/04 , C22F1/18 , C30B15/08 , C30B29/02 , C30B29/52
摘要: The present invention provides a metal wire rod composed of iridium or an iridium alloy, wherein the number of crystal grains on any cross-section in a longitudinal direction is 2 to 20 per 0.25 mm2, and the Vickers hardness at any part is 200 Hv or more and less than 400 Hv. The iridium wire rod is a material which is produced by a μ-PD method, and has low residual stress and which has a small change in the number of crystal grains and hardness even when heated to a temperature equal to or higher than a recrystallization temperature (1200° C. to 1500° C.). The metal wire rod of the present invention is excellent in oxidative consumption resistance under a high-temperature atmosphere, and mechanical properties.
摘要翻译: 本发明提供一种由铱或铱合金构成的金属线材,其中纵向方向的任何截面上的晶粒数为2〜20 / 0.25mm 2,任何部分的维氏硬度为200Hv或 多于400 Hv。 铱线棒是通过μ-PD法制造的材料,残留应力低,即使在加热到再结晶温度以上的温度下,晶粒数和硬度也有小的变化 (1200℃〜1500℃)。 本发明的金属线棒在高温环境下的耐氧化消耗性优异,机械性能优良。
-
公开(公告)号:US20170130310A1
公开(公告)日:2017-05-11
申请号:US15127348
申请日:2015-03-23
发明人: Kiyohito ISHIDA , Toshihiro OMORI , Yutaka SATO , Kunihiro TANAKA , Muneki NAKAMURA , Koichi SAKAIRI , Tatsuya NAKAZAWA
CPC分类号: C22F1/10 , C22C19/03 , C22C19/055 , C22C19/056 , C22C30/00
摘要: The present invention relates to a NiIr-base heat-resistant alloy which includes a Ni—Ir—Al—W-base alloy which contains Ir: 5.0 to 50.0 mass %, Al: 1.0 to 8.0 mass %, W: 5.0 to 20.0 mass %, and the balance is Ni, and a γ′ phase having an L12 structure precipitating and dispersing in a matrix as an essential strengthening phase, and a ratio (Y/X) of a peak intensity (Y) of (201) plane of the Ir3W phase observed in the range of 2θ=48° to 50° to a peak intensity (X) of (111) plane of the γ′ phase observed in the range of 2θ=43° to 45° in X-ray diffraction analysis is 0.5 or less. The alloy exhibits good high-temperature property stably.
-
公开(公告)号:US20160040276A1
公开(公告)日:2016-02-11
申请号:US14774223
申请日:2014-03-11
发明人: Kiyohito ISHIDA , Toshihiro OMORI , Yutaka SATO , Kunihiro TANAKA , Muneki NAKAMURA , Koichi SAKAIRI
摘要: The present invention is a heat-resistant Ni-base alloy including a Ni—Ir—Al—W alloy having essential additive elements of Ir, Al, and W added to Ni, wherein the heat-resistant Ni-base alloy includes Ir: 5.0 to 50.0 mass %, Al: 1.0 to 8.0 mass %, and W: 5.0 to 20.0 mass %, the balance being Ni, and a γ′ phase having an L12 structure disperses in a matrix as an essential strengthening phase. The heat-resistant material including the Ni-base alloy may contain one or more additive elements selected from B: 0.001 to 0.1 mass %, Co: 5.0 to 20.0 mass %, Cr: 1.0 to 25.0 mass %, Ta: 1.0 to 10.0 mass %, Nb: 1.0 to 5.0 mass %, Ti: 1.0 to 5.0 mass %, V: 1.0 to 5.0 mass %, and Mo: 1.0 to 5.0 mass %, or 0.001 to 0.5 mass % of C.
摘要翻译: 本发明是一种耐Ni基合金,其中Ni-Ir-Al-W合金具有添加到Ni中的Ir,Al和W的重要添加元素,其中耐热Ni基合金包括Ir:5.0 至50.0质量%,Al:1.0〜8.0质量%,W:5.0〜20.0质量%,余量为Ni,具有L12结构的γ'相分散在基质中作为必需的强化相。 包含Ni基合金的耐热材料可以含有选自B:0.001〜0.1质量%,Co:5.0〜20.0质量%,Cr:1.0〜25.0质量%,Ta:1.0〜10.0质量% %,Nb:1.0〜5.0质量%,Ti:1.0〜5.0质量%,V:1.0〜5.0质量%,Mo:1.0〜5.0质量%,或0.001〜0.5质量%。
-
-