公开(公告)号：US20150243403A1

公开(公告)日：2015-08-27

申请号：US14624760

申请日：2015-02-18

申请人： TITAN KOGYO KABUSHIKI KAISHA

发明人： Yasuo INOUE ,  Shigeru Nagaoka ,  Misao Mazaki ,  Hiromasa Kondoh ,  Eisuke Yoshioka

IPC分类号： H01B1/08 ,  C09D5/24 ,  H01B13/00 ,  H01B1/20

CPC分类号： H01B1/08 ,  B82Y30/00 ,  C01G23/047 ,  C01P2002/52 ,  C01P2004/04 ,  C01P2004/16 ,  C01P2004/84 ,  C01P2006/12 ,  C01P2006/40 ,  C01P2006/60 ,  C09C1/3661 ,  C09D5/24 ,  H01B1/20 ,  H01B13/0026

摘要： Fine powder of transparent conductive oxide composites is obtained by covering a surface of a rod-like rutile-type titanium oxide particle having a long axis diameter of 0.05 μm or higher and 0.15 μm or lower, a short axis diameter of 0.01 μm or higher and lower than 0.03 μm, and an axis ratio of 5 or higher, with a doped tin oxide using a wet method, wherein antimony is doped at 10 to 25 wt % as Sb against SnO2, at 1 to 2 wt %/m2 per a specific surface area of the substrate; and firing the substrate under an oxidizing atmosphere at a firing temperature of 400 to 700° C.

摘要翻译： 通过覆盖长轴直径为0.05μm以上且0.15μm以下，短轴直径为0.01μm以上的棒状金红石型氧化钛粒子的表面，得到透明导电性氧化物复合体的细粉末， 低于0.03μm，轴比为5以上，与使用湿法的掺杂氧化锡相比，其中锑以SnO 2为10〜25重量％，以SnO 2的比例掺杂，以1〜2重量％/ m 2 基材的表面积; 在400〜700℃的烧成温度下，在氧化气氛下烧成。