公开(公告)号：US4354877A

公开(公告)日：1982-10-19

申请号：US202786

申请日：1980-10-31

申请人： Toshio Kawano ,  Shiro Ishii ,  Koichi Soeda ,  Jyunichiro Migita

发明人： Toshio Kawano ,  Shiro Ishii ,  Koichi Soeda ,  Jyunichiro Migita

IPC分类号： C09K3/00 ,  B02C19/18 ,  C04B7/00 ,  C04B28/10 ,  C04B41/00 ,  E04G23/08 ,  E21C37/00 ,  E21C37/12 ,  F42D3/00 ,  F42D99/00 ,  C04B7/02

CPC分类号： F42D3/00 ,  C04B28/10 ,  C04B41/0009 ,  C04B7/00 ,  E04G23/08 ,  E21C37/12

摘要： A demolition agent which acts by means of expansive stress generated upon hydration and which is prepared by calcining limestone at 1300.degree. to 1600.degree. C. to produce a hard-burned quick lime whose crystal sizes are 10 to 100 micron, pulverizing the resulting hard-burned quick lime to 1500 to 5000 cm.sup.2 /g (Blaine), mixing 5 to 70 parts by weight of a hydraulic material to 30 to 95 parts by weight of the hard-burned quick lime and furthermore adding 0.1 to 5 parts by weight of an admixture comprising a water reducing agent to 100 parts by weight of the mixture of the powdery hard-burned quick lime and the hydraulic material.The demolition agent is used as an aqueous slurry. The slurry is filled into holes of a brittle material to demolish the brittle material by means of expansive stress generated upon hydration.

摘要翻译： 通过在水合时产生的膨胀应力作用的破坏剂，其通过在1300℃至1600℃煅烧石灰石制备，以产生晶体尺寸为10至100微米的硬烧的生石灰，粉碎所得的硬质合金， 将生石灰烧成1500〜5000cm2 / g（Blaine），将5〜70重量份的水硬性材料与30〜95重量份的硬烧生石灰混合，再加入0.1〜5重量份 包含减水剂的混合物至100重量份的粉状硬烧的生石灰与水硬性材料的混合物。 拆除剂用作含水浆料。 将浆料填充到脆性材料的孔中，以通过在水合时产生的膨胀应力来破坏脆性材料。