公开(公告)号：WO2007126061A1

公开(公告)日：2007-11-08

申请号：PCT/JP2007/059190

申请日：2007-04-27

Applicant: 松下電器産業株式会社 ,  福井 裕介 ,  辻田 卓司 ,  橋本 潤 ,  西谷 輝 ,  寺内 正治 ,  西谷 幹彦

Inventor： 福井 裕介 ,  辻田 卓司 ,  橋本 潤 ,  西谷 輝 ,  寺内 正治 ,  西谷 幹彦

IPC: H01J11/02 ,  H01J9/02

CPC classification number: H01J11/40 ,  H01J9/02 ,  H01J11/12 ,  H01J11/38

Abstract: Provided is a PDP capable of exhibiting electric charge holding characteristic in a protection layer while driving the PDP with a low voltage and exhibiting a preferable image display characteristic. Moreover, in addition to the aforementioned effects, it is possible to prevent generation of discharge delay and preferably perform high-speed drive even in a highly fine PDP, thereby realizing a high-quality image display. As means for realizing this, a surface layer (8) formed under an oxygen atmosphere of oxygen partial pressure of 0.025 Pa or above and having a film thickness of about 1 µm is arranged on the discharge space side of a dielectric layer (7). Furthermore, on the surface of the surface layer (8), MgO minute particles (16) are dispersed. The surface layer (8) protects the dielectric layer (7) from ion bombardment during discharge, reduces the discharge start voltage, and improves the charge missing. Moreover, the MgO minute particles (16) exhibit a high initial electron emission characteristic.

Abstract translation: 提供了一种能够在保护层中显示电荷保持特性的PDP，同时以低电压驱动PDP并且具有优选的图像显示特性。 此外，除了上述效果之外，即使在高度精细的PDP中也能够防止放电延迟的产生，并且优选地执行高速驱动，从而实现高质量的图像显示。 作为实现这一点的手段，在电介质层（7）的放电空间侧配置有在氧分压为0.025Pa以上且膜厚约1μm的氧气氛下形成的表面层（8）。 此外，在表层（8）的表面上分散MgO微粒（16）。 表面层（8）在放电期间保护电介质层（7）免受离子轰击，降低放电起始电压，并改善电荷缺失。 此外，MgO微粒（16）表现出高的初始电子发射特性。

公开(公告)号：WO2008047910A1

公开(公告)日：2008-04-24

申请号：PCT/JP2007/070452

申请日：2007-10-19

Applicant: 松下電器産業株式会社 ,  寺内 正治 ,  福井 裕介 ,  辻田 卓司 ,  岡藤 美智子 ,  西谷 幹彦

Inventor： 寺内 正治 ,  福井 裕介 ,  辻田 卓司 ,  岡藤 美智子 ,  西谷 幹彦

IPC: H01J11/02

CPC classification number: H01J11/40 ,  H01J9/02 ,  H01J11/12

Abstract: 　本発明は、保護層における放電特性を改善することにより、高精細セル構造においても優れた画像表示性能を発揮することが可能なＰＤＰとその製造方法を提供することを目的とするものである。 　具体的には、保護層８をＭｇＯ膜層８１と、ＭｇＯ結晶粒子群１６からなるＭｇＯ結晶粒子層８２で構成する。ＭｇＯ結晶粒子群１６は、ＭｇＯ前駆体焼成による作製方法に基づき、ＣＬ測定における６５０ｎｍ以上９００ｎｍ未満の波長領域のスペクトル積分値をａ、３００ｎｍ以上５５０ｎｍ未満の波長領域のスペクトル積分値をｂとするとき、比率ａ／ｂが１．２以上である特性を持つように作製する。

Abstract translation: 公开了具有改善的放电特性的保护层的PDP，因此即使PDP具有高分辨率的单元结构，也能够显示出优异的图像显示性能。 还公开了一种用于制造PDP的方法。 具体地，保护层（8）由MgO膜层（81）和包含MgO结晶粒子（16）的MgO结晶粒子层（82）构成。 按照a / b比为1.2以上的方式，按照MgO前体烧成的制造方法制备MgO结晶粒子（16），其中，“a”表示波长范围内的光谱积分值 小于650nm且小于900nm，并且在确定CL时，“b”表示在不小于300nm且小于550nm的波长范围内的光谱积分值。

公开(公告)号：WO2007139183A1

公开(公告)日：2007-12-06

申请号：PCT/JP2007/061078

申请日：2007-05-31

Applicant: 松下電器産業株式会社 ,  福井 裕介 ,  寺内 正治 ,  辻田 卓司

Inventor： 福井 裕介 ,  寺内 正治 ,  辻田 卓司

IPC: H01J11/02 ,  H01J17/16 ,  C01F5/08 ,  C30B29/60

CPC classification number: H01J11/40 ,  C01F5/02 ,  C01F5/06 ,  C01F5/08 ,  C01F5/12 ,  C01P2002/77 ,  C01P2002/90 ,  C01P2004/03 ,  C01P2004/38 ,  C01P2004/41 ,  C01P2004/52 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2006/80 ,  H01J9/02 ,  H01J11/12

Abstract: This invention is directed to modification of a protective layer to solve both problems of "discharge delay" and "temperature dependency of discharge delay" while realizing good drive at low voltage. There is also provided a plasma display panel, which can realize excellent display properties, by solving the above problems and, further, suppressing "dependency of discharge delay upon space charge". An alkoxide of magnesium having a purity of not less than 99.95% (Mg(OR) 2 ) or acetylacetone of magnesium having a purity of not less than 99.95% is provided. A small amount of acid is added to this aqueous solution for hydrolysis to prepare a gel of magnesium hydroxide as an MgO precursor. The gel is fired in the air at a temperature of 1500°C or above to prepare a powder containing MgO fine particles (16a to 16d) having an NaCl crystal structure surrounded by (100) face and (111) face. The powder is coated on the dielectric layer (7) or surface layer (8) to form a group of MgO fine particles (16).

Abstract translation: 本发明涉及在低电压下实现良好驱动的同时解决“放电延迟”和“放电延迟的温度依赖性”两个问题的保护层的改进。 还提供了一种通过解决上述问题并进一步抑制“放电延迟对空间充电的依赖性”而能够实现优异的显示特性的等离子体显示面板。 提供纯度为99.95％以上的镁的醇盐（Mg（OR）2））或纯度为99.95％以上的镁的乙酰丙酮。 向该水溶液中加入少量酸进行水解以制备作为MgO前体的氢氧化镁凝胶。 将凝胶在空气中在1500℃以上的温度下烧成，制备含有由（100）面和（111）面包围的NaCl晶体结构的MgO微粒（16a〜16d）的粉末。 粉末涂覆在电介质层（7）或表面层（8）上以形成一组MgO微粒（16）。

公开(公告)号：WO2008047911A1

公开(公告)日：2008-04-24

申请号：PCT/JP2007/070453

申请日：2007-10-19

Applicant: 松下電器産業株式会社 ,  辻田 卓司 ,  福井 裕介 ,  寺内 正治 ,  西谷 幹彦 ,  岡藤 美智子 ,  石野 真一郎 ,  溝上 要

Inventor： 辻田 卓司 ,  福井 裕介 ,  寺内 正治 ,  西谷 幹彦 ,  岡藤 美智子 ,  石野 真一郎 ,  溝上 要

IPC: H01J11/02

CPC classification number: H01J11/12 ,  H01J9/02 ,  H01J11/40

Abstract: 　本発明は、保護層における放電特性を改善することにより、高精細セル構造においても優れた画像表示性能を発揮することが可能なＰＤＰとその製造方法を提供するものである。 　具体的には、保護層８をＭｇＯ膜層８１と、ＭｇＯ結晶粒子群１６からなるＭｇＯ結晶粒子層８２で構成する。ＭｇＯ結晶粒子群１６は、ＭｇＯ前駆体焼成による作製方法に基づき、ＣＬ測定における２００ｎｍ以上３００ｎｍ未満の波長領域のスペクトル積分値をａ、３００ｎｍ以上５５０ｎｍ未満の波長領域のスペクトル積分値をｂとするとき、比率ａ／ｂが１以上である特性を持つように作製する。

Abstract translation: 公开了具有改善的放电特性的保护层的PDP，因此即使PDP具有高分辨率的单元结构，也能够显示出优异的图像显示性能。 还公开了一种用于制造PDP的方法。 具体地，保护层（8）由MgO膜层（81）和包含MgO结晶粒子（16）的MgO结晶粒子层（82）构成。 按照a / b比为1以上的方式，按照MgO前驱体烧制的制造方法制备MgO结晶粒子（16），其中，“a”表示波长范围内的光谱积分值 小于200nm且小于300nm，并且在确定CL时，“b”表示在不小于300nm且小于550nm的波长范围内的光谱积分值。

公开(公告)号：WO2007139184A1

公开(公告)日：2007-12-06

申请号：PCT/JP2007/061079

申请日：2007-05-31

Applicant: 松下電器産業株式会社 ,  福井 裕介 ,  寺内 正治 ,  辻田 卓司

Inventor： 福井 裕介 ,  寺内 正治 ,  辻田 卓司

IPC: H01J11/02 ,  H01J17/16 ,  H01J9/02 ,  C01F5/08 ,  C30B29/60

CPC classification number: H01J11/40 ,  C01F5/02 ,  C01F5/06 ,  C01F5/08 ,  C01F5/12 ,  C01P2002/77 ,  C01P2002/90 ,  C01P2004/03 ,  C01P2004/38 ,  C01P2004/41 ,  C01P2004/52 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2006/80 ,  H01J9/02 ,  H01J11/12

Abstract: This invention is directed to modification of a protective layer to solve both problems of "discharge delay" and "temperature dependency of discharge delay" while realizing good drive at low voltage. There is also provided a plasma display panel, which can realize excellent display properties, by solving the above problems and, further, suppressing "dependency of discharge delay upon space charge". An alkoxide of magnesium having a purity of not less than 99.95% (Mg(OR) 2 ) or acetylacetone of magnesium having a purity of not less than 99.95% is provided. A small amount of acid is added to this aqueous solution for hydrolysis to prepare a gel of magnesium hydroxide as an MgO precursor. The gel is fired in the air at a temperature of 700°C or above to prepare a powder containing MgO fine particles (16a to 16d) having an NaCl crystal structure surrounded by (100) face, (110) face and (111) face. The powder is coated on the dielectric layer (7) or surface layer (8) to form a group of MgO fine particles (16).

Abstract translation: 本发明涉及在低电压下实现良好驱动的同时解决“放电延迟”和“放电延迟的温度依赖性”两个问题的保护层的改进。 另外，通过解决上述问题，还能够抑制“放电延迟对空间充电的依赖性”，能够实现优异的显示特性。 提供纯度为99.95％以上的镁的醇盐（Mg（OR）2））或纯度为99.95％以上的镁的乙酰丙酮。 向该水溶液中加入少量酸进行水解以制备作为MgO前体的氢氧化镁凝胶。 将凝胶在700℃以上的温度下在空气中烧成，制作含有由（100）面，（110）面和（111）面包围的具有NaCl晶体结构的MgO微粒（16a〜16d）的粉末 。 粉末涂覆在电介质层（7）或表面层（8）上以形成一组MgO微粒（16）。