There is provided a joined product suitable as a cutting tool that is fit for high-speed cutting, CVD coating process and the like, and does not cause a reduction in joint strength of a joining layer even if a high temperature exceeding a temperature at which a brazing filler forms the liquid phase is reached during cutting. Specifically, the joined product includes a cemented carbide sintered compact serving as a first material to be joined and a cBN sintered compact or a diamond sintered compact serving as a second material to be joined. The first material to be joined and the second material to be joined are joined by a joining material that does not form a liquid phase at a temperature lower than 1000° C. and that is placed between the first material to be joined and the second material to be joined. The joining is performed by resistance heating and pressing at a pressure of 0.1 to 200 MPa.