An environmentally degradable composite having between 20 and 80 weight parts of a moderately cross-linked copolymer of aliphatic polyesteramide comprising random blocks, between 10 and 70 weight parts of a renewable raw material, between 5 and 20 weight parts of an additive, and between 0 and 30 weight parts of a filler. The composite has good mechanical properties, with a tensile strength of between 15 and 30 MPa, elongation at break of between 300 and 1000%, bending strength of between 10 and 25 MPa, and notched impact strength of between 20 and 90 kJ/m2. The composite has good environmental degradability and after 12 weeks' composting, the biodegradation rate thereof exceeds 90%. The composite has good formation performance, and can be processed using conventional plastics processing equipment by extruding, injection molding, blow molding, and hot pressing for preparation of a variety of products.