公开(公告)号：EP2927202A1

公开(公告)日：2015-10-07

申请号：EP14305495.5

申请日：2014-04-04

申请人： Paris Sciences et Lettres - Quartier Latin

发明人： Mortier, Michel ,  Aballea, Pierre ,  Gredin, Patrick ,  Suganuma, Akiko

IPC分类号： C04B35/553 ,  C04B35/626

CPC分类号： C04B35/553 ,  C04B35/62615 ,  C04B35/6263 ,  C04B35/6264 ,  C04B35/62655 ,  C04B35/6266 ,  C04B35/64 ,  C04B2235/3201 ,  C04B2235/3206 ,  C04B2235/3208 ,  C04B2235/3213 ,  C04B2235/3215 ,  C04B2235/3224 ,  C04B2235/3225 ,  C04B2235/3227 ,  C04B2235/3241 ,  C04B2235/3279 ,  C04B2235/5454 ,  C04B2235/5481 ,  C04B2235/6562 ,  C04B2235/6565 ,  C04B2235/6567 ,  C04B2235/658 ,  C04B2235/668 ,  C04B2235/77 ,  C04B2235/781 ,  C04B2235/784 ,  C04B2235/785 ,  C04B2235/9653

摘要： A method for producing a metal fluoride ceramic, comprising: providing a sedimented compound comprising metal fluoride particles having an average particle size lower than 30 nm and a solvent, partially drying the sedimented compound at a temperature lower than 65°C until the partially dried compound comprises from 5 wt% to 45 wt% of the solvent, and sintering, for example in air, the partially dried and sedimented compound. The resulting ceramic is a transparent metal fluoride ceramic having an average grain size lower than 450 nm and having an absorbance lower than 0.05 cm -1 at 1200 nm and lower than 1 cm -1 at 370 nm. Preferably calcium fluoride is used.

摘要翻译： 一种金属氟化物陶瓷的制造方法，其特征在于，包括：提供包含平均粒径小于30nm的金属氟化物粒子和溶剂的沉降化合物，在低于65℃的温度下部分干燥沉淀化合物直到部分干燥的化合物 包括5重量％至45重量％的溶剂，并且例如在空气中烧结部分干燥和沉淀的化合物。 得到的陶瓷是平均粒径低于450nm，吸光度在1200nm处低于0.05cm -1且在370nm处低于1cm -1的透明金属氟化物陶瓷。 优选使用氟化钙。