公开(公告)号：KR1020100087472A
公开(公告)日：2010-08-05
申请号：KR1020090006480
申请日：2009-01-28
Applicant: 현대제철 주식회사
Inventor： 고강희
CPC classification number: C21D8/0294 , B21B1/22
Abstract: PURPOSE: A method for preventing surface cracks of a hot rolling process is provided to prevent crack through re-rolling and heat treatment and to roll a single blank material with variation in thickness. CONSTITUTION: A method for preventing surface cracks of a hot rolling process comprises the steps of: firstly rolling a part of a material to have variation in thickness, performing heat treatment of the part of the material at 900~1100°C so as to remove stress and induce recrystallization of grains, and re-rolling the heat-treated part of the material. In the heat treatment step, the rest part is cooled to 20~200°C in order to prevent recrystallization.
Abstract translation: 目的：提供一种防止热轧工艺的表面裂纹的方法，以防止通过再轧和热处理的裂纹，并且轧制厚度变化的单一坯料。 构成：用于防止热轧过程的表面裂纹的方法包括以下步骤：首先将材料的一部分轧制以具有厚度变化，在900〜1100℃下对材料的一部分进行热处理以除去 应力并引起晶粒的再结晶，并重新轧制材料的热处理部分。 在热处理工序中，将其余部分冷却至20〜200℃，以防再结晶。
-
公开(公告)号：KR1020150080783A
公开(公告)日：2015-07-10
申请号：KR1020140000260
申请日：2014-01-02
Applicant: 한양대학교 에리카산학협력단
CPC classification number: C21D8/0263 , C21D1/18 , C21D8/0294 , C21D2211/005 , C21D2221/00
Abstract: 열연강판의제조방법이설명된다. 상기방법은, 슬라브를열간압연하는열간압연단계, 열간압연된상기슬라브의표면을냉각하여, 상기슬라브의표면부의조직을상 변태시키는제1 상변태단계, 상기슬라브의상기표면부의조직을상 변태시킨후, 상기슬라브의중심부의조직을상 변태시키는제2 상변태단계, 및상 변태된상기표면부및 상기중심부를포함하는상기슬라브를권취하는권취단계를포함한다.
Abstract translation: 对热轧钢板的制造方法进行说明。 该方法包括热轧轧制板坯的热轧步骤; 通过冷却板坯的表面部分来变形热轧板坯的表面部分的组织的第一相变质步骤; 在变形板坯表面部分的组织之后，变形板坯中心部分的组织的第二相变形步骤; 以及卷绕包括变质表面部分和中心部分的板的卷绕步骤。
-
公开(公告)号：KR1020170121282A
公开(公告)日：2017-11-01
申请号：KR1020177027739
申请日：2016-03-16
Applicant: 닛신 세이코 가부시키가이샤
IPC: C22C38/40 , C22C38/58 , C22C38/02 , C21D9/46 , C21D8/02 , B21B1/22 , G11B33/02 , G11B33/14 , C21D1/76
CPC classification number: B21B1/22 , B21B1/227 , C21D1/76 , C21D6/002 , C21D8/0236 , C21D8/0273 , C21D8/0294 , C21D9/46 , C21D2211/001 , C22C38/001 , C22C38/02 , C22C38/04 , C22C38/40 , C22C38/42 , C22C38/44 , C22C38/58 , C23C8/14 , C23C8/18 , G11B33/02 , G11B33/14
Abstract: 세정성, 방현성및 친수성이우수한오스테나이트계스테인리스강판을제공한다. 마무리냉간압연및 광휘소둔후에덜롤을이용하여조질압연한오스테나이트계스테인리스강판에있어서, 강판표면에있어서의압연방향에대하여수직인방향의산술평균거칠기(Ra)가 0.2㎛이상 1.2㎛이하이다. 또, 강판표면에있어서의덜 모양의전사율이 15% 이상 70% 이하이다. 또한, 강판표면에형성된깊이가 0.5㎛이상이고개구면적이 10μ㎡이상인마이크로피트는, 존재밀도가 0.01㎟당 10.0개이하이며, 한편, 개구부면적률이 1.0% 이하이다. 또, 강판표면에형성된피막은, C 이외의피막형성원소로서, 적어도 Si와, N과, Al과, Mn과, Cr과, Fe와, Nb와, Ti와, O를함유하고, 또한, Si 함유량이 10원자% 이상이고, N 함유량이 10원자% 이하인 SiO주체의산화물로구성한다.
Abstract translation: 提供了清洁性，阻燃性和亲水性优异的奥氏体不锈钢板。 在精冷轧和用调质退火deolrol一个轧后的光泽的奥氏体不锈钢板，它是算术平均的方向上的粗糙度（Ra）为垂直于或小于1.2㎛0.2㎛到钢板表面的轧制方向。 另外，钢板表面上的较少形状的转印率为15％以上且70％以下。 此外，深度是形成在钢板的表面上和微坑不大于所述开口面积10μ㎡少，存在的大于10.0每0.01㎟密度上大于0.5㎛，在另一方面，开口面积率超过1.0％。 形成在钢板的表面上的涂层，作为C以外的成膜元素，至少含有Si，N和，Al和，Mn和，Cr和，Fe和Nb及含有Ti和O，也，硅 10原子％以上的含量和10原子％以下的N含量。
-
公开(公告)号：KR1020160115762A
公开(公告)日：2016-10-06
申请号：KR1020160034436
申请日：2016-03-23
Applicant: 베바 베르크초익바우 베트립스 게엠베하
CPC classification number: C21D1/06 , B21D22/022 , B21D24/16 , B21D35/001 , B21D53/88 , C21D1/673 , C21D8/005 , C21D8/0294 , C21D8/0405 , C21D9/0068 , C21D9/48 , B21D22/208 , B21D22/26 , B21D37/16
Abstract: 본발명은, 경화성열간성형가능강판으로구성된반제품(19)을경화온도로가열하는단계; 가열된반제품(19)을조합된열간성형절단장치내에서 3차원성형부품(20)으로열간성형하는단계; 조합된열간성형절단장치내에서성형부품(20)을절단하는단계; 제1 부분영역(21A)이급속냉각에의해경화되고, 성형부품(20)의제2 부분영역(21B)이제1 부분영역(21A)보다더 큰연성과더 낮은강도를갖게열 처리되도록, 열간성형절단장치내에서성형부품(20)을경화된성형부품(20)으로가압경화하는단계를포함하며, 성형부품의절단작업은적어도제1 및제2 부분영역(21A, 21B) 중하나에서실시되는, 부분적으로경화된금속성형부품의제조프로세스에관한것이다. 또한, 본발명은금속성형부품을제조하기위한조합된열간성형절단장치(2)에관한것이다.
-
公开(公告)号：KR1020180074148A
公开(公告)日：2018-07-03
申请号：KR1020160177937
申请日：2016-12-23
Applicant: 주식회사 포스코
CPC classification number: C21D8/02 , C22C38/02 , C22C38/06 , C22C38/22 , C22C38/28 , C22C38/38 , C22C38/60 , C21D8/0221 , C21D8/0247 , C21D8/0294 , C21D2211/005 , C21D2211/008
Abstract: 본발명은기존미니밀공정의문제점을극복하기위해연주~압연직결공정에서연연속압연모드를이용하여표면품질이우수할뿐만아니라강판의폭, 길이방향재질편차를현저히감소시킨인장강도 780MPa급고강도열연강판및 그제조방법을제공하기위함이다.
-
Patent Agency Ranking
公开(公告)号：KR20180054659A
公开(公告)日：2018-05-24
申请号：KR20187009375
申请日：2016-08-11
Applicant: AKTIEN GES DER DILLINGER HUETTENWERKE
Inventor： BALDAUF BERND , WILD DANIEL , RUPP DANIEL
CPC classification number: C23C8/66 , B22F1/00 , C21D1/74 , C21D6/00 , C21D8/0226 , C21D8/0294 , G01N29/30
Abstract: 본발명은, 특히강철또는다른금속으로부터형성된, 분석방법용교정바디를제조하기위한방법에관한것이다. 본발명에따라, 교정바디는분석방법에의해분석될제품을제조하기위해제공된재료로부터형성되고, 그재료로부터형성된반제품(1)의적어도하나의영역(9, 11, 12)에서그 재료의특성이변경된다. 바람직하게, 재료특성은다만표면에가까우면서일 표면(5, 2, 3, 4)으로부터반제품내부로연장되는영역(9, 11, 12)에서만변경되며, 이경우에는바람직하게재료특성을변경하는물질이반제품(1) 내부의영역(9, 11, 12) 내로주입된다. 또한, 본발명은, 교정바디및 교정바디의용도와도관련이있다.
-
公开(公告)号：KR1020170121276A
公开(公告)日：2017-11-01
申请号：KR1020177027620
申请日：2016-03-16
Applicant: 닛신 세이코 가부시키가이샤
IPC: C22C38/26 , C22C38/28 , C22C38/02 , C22C38/04 , C22C38/20 , C21D8/02 , B21B1/22 , B21B3/02 , G11B33/08 , G11B33/14
CPC classification number: B21B1/22 , B21B3/02 , B21B2001/221 , B21B2001/228 , B21B2201/04 , B21B2261/04 , B21B2261/14 , C21D1/76 , C21D8/0236 , C21D8/0273 , C21D8/0294 , C21D9/46 , C21D2211/005 , C22C38/001 , C22C38/004 , C22C38/02 , C22C38/04 , C22C38/06 , C22C38/12 , C22C38/16 , C22C38/18 , C22C38/20 , C22C38/26 , C22C38/28 , C22C38/32 , C22C38/34 , C22C38/40 , C23C8/02 , C23C8/10 , C23C8/18 , C23C8/60 , G11B33/08 , G11B33/14
Abstract: 세정성, 방현성및 친수성이우수한페라이트계스테인리스강판을제공한다. 마무리냉간압연및 광휘소둔후에덜롤을이용하여조질압연한페라이트계스테인리스강판에있어서, 강판표면에있어서의압연방향에대하여수직인방향의산술평균거칠기(Ra)가 0.2㎛이상 1.2㎛이하이다. 또, 강판표면에있어서의덜 모양의전사율이 15% 이상 70% 이하이다. 또한, 강판표면에형성된깊이가 0.5㎛이상이고개구면적이 10μ㎡이상인마이크로피트는, 존재밀도가 0.01㎟당 10.0개이하이며, 또한, 개구부면적률이 1.0% 이하이다. 또, 강판표면에형성된피막은, C 이외의피막형성원소로서, 적어도 Si와, N과, Al과, Mn과, Cr과, Fe와, Nb와, Ti와, O를함유하고, 또한, Si 함유량이 10원자% 이상이고, N 함유량이 10원자% 이하인 SiO주체의산화물로구성한다.
Abstract translation: 提供清洁性，可燃性和亲水性优异的铁素体不锈钢板。 在精加工冷轧并用回火后deolrol轧制光亮退火的铁素体不锈钢板，算术平均在垂直于或小于1.2㎛0.2㎛到钢板表面的轧制方向的方向上的粗糙度（Ra）为。 另外，钢板表面上的较少形状的转印率为15％以上且70％以下。 此外，深度是形成在钢板和微坑不大于所述开口面积10μ㎡更少的表面上超过0.5㎛是，的存在和大于10.0每0.01㎟密度，并且是开口面积比为1.0％或更低。 形成在钢板的表面上的涂层，作为C以外的成膜元素，至少含有Si，N和，Al和，Mn和，Cr和，Fe和Nb及含有Ti和O，也，硅 10原子％以上的含量和10原子％以下的N含量。
-
公开(公告)号：KR101583899B1
公开(公告)日：2016-01-13
申请号：KR1020140000260
申请日：2014-01-02
Applicant: 한양대학교 에리카산학협력단
CPC classification number: C21D8/0263 , C21D1/18 , C21D8/0294 , C21D2211/005 , C21D2221/00
Abstract: 열연강판의제조방법이설명된다. 상기방법은, 슬라브를열간압연하는열간압연단계, 열간압연된상기슬라브의표면을냉각하여, 상기슬라브의표면부의조직을상 변태시키는제1 상변태단계, 상기슬라브의상기표면부의조직을상 변태시킨후, 상기슬라브의중심부의조직을상 변태시키는제2 상변태단계, 및상 변태된상기표면부및 상기중심부를포함하는상기슬라브를권취하는권취단계를포함한다.
-
公开(公告)号：KR1020150012205A
公开(公告)日：2015-02-03
申请号：KR1020140092366
申请日：2014-07-22
Applicant: 주식회사 포스코
CPC classification number: C21D9/46 , B21B1/22 , B23K26/362 , B23K26/40 , B23K2203/04 , C21D6/008 , C21D8/0205 , C21D8/0247 , C21D8/0294 , C21D8/1277 , C21D8/1294 , C21D10/00 , C22C38/00 , C22C38/02
Abstract: 방향성 전기강판 및 그 제조방법이 개시된다. 본 발명의 일 실시예에 의한 방향성 전기강판은, 1차 재결정 형성 전 또는 1차 재결정 형성 후의 전기강판을 제공하는 단계; 및 상기 전기강판에 레이저를 조사 및 가스를 분사하여 전기강판의 표면에 그루브를 형성하는 단계를 포함하되, 상기 조사되는 레이저의 에너지 밀도(E
d ) 및 레이저의 주사속도(V
s )는 아래의 조건을 만족하는 것 일 수 있다.
1.0 J/mm
2 ≤ E
d ≤ 5.0J/mm
2 ,
0.0518mm/μsec≤ V
s ≤ 0.2mm/μsecAbstract translation: 公开了一种晶粒取向电工钢板及其制造方法。 根据本发明的实施方案的晶粒取向电工钢板的制造方法包括以下步骤：在形成一次再结晶之前或之后提供电工钢板; 并且通过向电工钢板照射激光并将气体喷射到其上而在电工钢板上形成槽，其中照射的激光束的能量密度（Ed）和扫描速度（Vs）满足以下条件 1.0J / mm2 <= Ed <= 5.0J / mm2，0.0518mm /μsec<= Vs <= 0.2mm /μsec。 根据本发明的优选实施例的提供的晶粒取向电工钢板通过在表面上形成凹槽来自我最小化。
-
公开(公告)号：KR1020130139847A
公开(公告)日：2013-12-23
申请号：KR1020137002753
申请日：2011-08-03
Applicant: 코스마 엔지니어링 유럽 아게
CPC classification number: B60R19/34 , B21D22/02 , B21D22/022 , B21D37/16 , B21D53/88 , B60R19/03 , B60R19/18 , B60R19/26 , B60R2019/1813 , B60R2019/182 , B60R2019/1826 , C21D1/673 , C21D8/0221 , C21D8/0294 , C21D9/46 , Y10T29/49622 , Y10T29/49826
Abstract: 빔 박스 충돌 관리 시스템 제조 방법은 제1 판금 블랭크로부터 제1 단일편 쉘(100a)을 열간 성형 처리로 형성하는 단계를 포함한다. 제1 쉘은 높은 인장 강도 빔 부분(102a)을 가지며, 빔 부분의 제1 끝단과 근접한 제1 낮은 항복 강도 크래시 박스 부분(104a) 및 빔 부분의 제2 끝단과 근접한 제2 낮은 항복 강도 크래시 박스 부분과 일체로 형성된다. 제1 쉘은 또한 빔 부분과 각각의 제1 및 제2 크래시 박스 부분(104a, 106a)을 따라서 연속적으로 연장되는 개방 측면을 가진다. 폐쇄 요소(100b)는 제2 판금 블랭크로부터 형성되며, 제1 쉘의 개방 측면에 근접하게 단단히 고정된다.
-
-
-
-
-
-
-
-
-