公开(公告)号：US06887309B2

公开(公告)日：2005-05-03

申请号：US10362519

申请日：2001-08-31

Applicant: Pascal Casanova ,  Hu Chong ,  Bernard Clavaud

Inventor： Pascal Casanova ,  Hu Chong ,  Bernard Clavaud

IPC: C04B7/52 ,  C04B20/00 ,  C04B28/02 ,  C04B14/48

CPC classification number: C04B7/527 ,  C04B20/008 ,  C04B28/02 ,  C04B2201/52 ,  Y02W30/92 ,  Y02W30/94 ,  C04B14/06 ,  C04B14/48 ,  C04B16/06 ,  C04B18/08 ,  C04B18/146 ,  C04B2103/32

Abstract: A concrete in which metallic fibers are dispersed, obtained through mixing with water a composition including a cement; ultrafine elements with a pozzolanic reaction; granular elements distributed into two granular classes (C1)>1 mm and

Abstract translation: 一种混合物，其中通过与水混合而获得金属纤维，所述组合物包括水泥; 具有火山灰反应的超细元素; 分布在两个粒度级别（C 1> 1）> 1mm和<5MM和（C 2 <2>）的颗粒状元素的范围为5至15mm; 水泥添加剂 在混合物中加入一定量的水E; 分散剂，优选为超增塑剂; 金属纤维，其最大等于120kg / m 3混凝土，各种组分（a），（b），（C 1 H 3）， （C 2/2），（d）和水的量E，以体积表示，满足以下关系：比1：0.50 <=（C 2/2）/（ C <1）<= 1.20; 比例2：0.25 <= [（A）+（B）+（D）] / [（C 1 H 2）+（C 2 N 2）] = 比3：0.10 <=（b）/（a）<= 0.30; 比例4：0.05 <= E / [（a）+（b）+（d）] <= 0.75; 比5：（d）/（a）<= 0.20。 本发明适用于没有框架，瓷砖和板，壳类型等的元件的制造。

公开(公告)号：US06881256B2

公开(公告)日：2005-04-19

申请号：US10203378

申请日：2001-02-08

Applicant: Gilles Orange ,  Evelyne Prat ,  Pascal Casanova ,  Mouloud Behloul

Inventor： Gilles Orange ,  Evelyne Prat ,  Pascal Casanova ,  Mouloud Behloul

IPC: C04B14/04 ,  C04B14/20 ,  C04B14/38 ,  C04B14/48 ,  C04B16/06 ,  C04B20/00 ,  C04B28/02

CPC classification number: C04B28/02 ,  C04B2111/28 ,  C04B2201/52 ,  Y02W30/94 ,  C04B14/06 ,  C04B14/20 ,  C04B14/465 ,  C04B14/48 ,  C04B16/0633 ,  C04B18/146 ,  C04B20/0076 ,  C04B40/0028 ,  C04B38/0051

Abstract: The invention concerns the use of organic fibers having a melting point lower than 300° C., an average length l more than 1 mm and a diameter Ø not more than 200 μm, in ultra high performance concrete for improving the concrete fire resistance, the amount of organic fibers being such that their volume ranges between 0.1 and 3% of the concrete volume after setting and the concrete having a compressive strength at 28 days of at least 120 Mpa, a bending strength of at least 20 Mpa, and a spread value in non-hardened state of at least 150 mm, the values being for a concrete preserved at 20° C., the concrete consisting of a particularly hardened cement matrix wherein metal fibres are dispersed.

Abstract translation: 本发明涉及在超高性能混凝土中使用熔点低于300℃，平均长度l大于1mm，直径不大于200μm的有机纤维，以提高混凝土耐火性， 有机纤维的数量使其体积在凝固后的混凝土体积的0.1至3％之间，混凝土在28天的抗压强度至少为120Mpa，弯曲强度为至少20Mpa，扩散值 在至少150mm的非硬化状态下，该值用于在20℃下保存的混凝土，该混凝土由特别硬化的水泥基质组成，其中金属纤维被分散。