摘要:
A ceramic filter comprising: (a) from about 75% to about 95% by weight of diatomaceous earth; (b) from about 10% to about 20% by weight of a flux; and (c) from about 0.03% to about 0.4% by weight of a metallic compound; the percentages by weight being percentages by weight of the ceramic filter.
摘要:
A spark plug which includes a center electrode metal shell and an insulator disposed therebetween utilizes for the insulator or ceramic with improved high temperature electrical properties which includes alumina in an amount between about 90 and about 99% by weight, a zirconium containing compound in an amount between about 0 and about 1% by weight, and an oxide mixture in an amount between about 1 and about 10% by weight. The oxide mixture includes a glass former, a network modifier and alumina in an amount between about 16% and about 40% by weight after firing, wherein the molar ratio of the glass former to the network modifier ranges between about 0.8:1 and 1.2:1. The ceramic insulator is particularly adapted for use as an insulator in a spark plug to provide improved dielectric strength and shunt resistance of greater than one 1000 megaohms at 1000 degrees Fahrenheit, so as to reduce the shunting of the spark plug and thereby improve the quality of the spark generated by the spark plug.
摘要:
An insulator including alumina in an amount between about 90 and about 99% by weight and an oxide mixture or glass mixture including Boron Oxide, Phosphorus Oxide, or both Boron and Phosphorus Oxide.
摘要:
A ceramic includes alumina in an amount between about 90 and about 99% by weight, a zirconium containing compound in an amount between about 0 and about 1% by weight, and an oxide mixture in an amount between about 1 and about 10% by weight. The oxide mixture includes a glass former and a network modifier, wherein the molar ratio of the glass former to the network modifier ranges between about 0.8:1 and 1.2:1. The ceramic insulator is particularly adapted for use as an insulator in a spark plug to provide improved dielectric strength and shunt resistance of greater than one 1000 megaohms at 1000 degrees Fahrenheit, so as to reduce the shunting of the spark plug and thereby improve the quality of the spark generated by the spark plug.
摘要:
A process is disclosed in which coarse silica, calcium oxides and magnesium oxides are treated in a ball mill together with grinding aids and cold-strength binders. This material is then agglomerated with water to produce a product that reacts at elevated temperatures, e.g. in a fluidized bed reactor, to produce synthetic silicates.