CPC分类号： C23C14/024 ,  B32B27/08 ,  B32B27/10 ,  B32B27/32 ,  B32B27/36 ,  B32B2255/28 ,  B32B2307/518 ,  C23C14/12 ,  C23C14/562 ,  Y10T428/1379 ,  Y10T428/1383 ,  Y10T428/24917 ,  Y10T428/2951 ,  Y10T428/2955 ,  Y10T428/31565 ,  Y10T428/31598 ,  Y10T428/31678 ,  Y10T428/31681 ,  Y10T428/31692 ,  Y10T428/31703 ,  Y10T428/31786 ,  Y10T428/31938 ,  Y10T428/31942 ,  Y10T428/31993 ,  Y10T428/31996

摘要： The invention relates to a laminate comprising two plastic films and in between a metal or metaloxide layer and a crystalline triazine layer, the laminate having a lamination strength of about 2 N/inch or more as measured in a 90 degree tensile testing at 30 mm/min. The invention further relates to a composite layer, comprising a metal or metal oxide, and a triazine layer comprising a triazine compound suitable for said laminate. The invention further relates to a process for the preparation of a composite layer, comprising the step of applying a triazine layer on a substrate with a metal or metal oxide layer by vapor deposition of the triazine compound, wherein the process comprises (a) applying to the metal or metal oxide layer a compound other than a triazine compound, (b) vapor depositing the triazine compound on the metal or metal oxide layer while the compound is at least in part in a liquid state.

摘要翻译： 本发明涉及一种包含两个塑料膜并且在金属或金属氧化物层和结晶三嗪层之间的层压体，所述层压板的层压强度为约20N /英寸或更大，在90度/ 分钟 本发明还涉及包含金属或金属氧化物的复合层和包含适用于所述层压体的三嗪化合物的三嗪层。 本发明还涉及一种制备复合层的方法，包括通过气相沉积三嗪化合物在金属或金属氧化物层上在基底上施加三嗪层的步骤，其中该方法包括（a）应用于 所述金属或金属氧化物层是三嗪化合物以外的化合物，（b）在所述化合物至少部分为液态的状态下，在所述金属或金属氧化物层上气相沉积所述三嗪化合物。