摘要:
Polyvinylidene fluoride resin powder for melt molding, which exhibits such particle size distribution characteristics that the average particle diameter (D50) is 80 to 250 μm, the proportion of resin powder having a particle diameter of at most 45 μm is at most 15.0% by weight, and the proportion of resin powder having a particle diameter of at least 355 μm is at most 10.0% by weight, and has a bulk density of 0.30 to 0.80 g/cm3 and an angle of repose of at most 40°, and a process for producing a molding, which comprises feeding the resin powder to an injection molding machine or extrusion molding machine, melting the resin powder, and injecting the resin melt into a mold.
摘要翻译:用于熔融成型的聚偏二氟乙烯树脂粉末,其具有平均粒径(D≤50)为80〜250μm的粒度分布特性,粒径为45以下的树脂粉末的比例 妈妈最多为15.0重量%,粒径至少为355μm的树脂粉末的比例为至多10.0重量%,堆积密度为0.30〜0.80g / cm 3, SUP>和休止角至多为40°,以及制造成型品的方法,其包括将树脂粉末进料到注塑机或挤出成型机中,熔化树脂粉末,并将树脂熔体注入模具 。
摘要:
Polyvinylidene fluoride resin powder for melt molding, which exhibits such particle size distribution characteristics that the average particle diameter (D50) is 80 to 250 μm, the proportion of resin powder having a particle diameter of at most 45 μm is at most 15.0% by weight, and the proportion of resin powder having a particle diameter of at least 355 μm is at most 10.0% by weight, and has a bulk density of 0.30 to 0.80 g/cm3 and an angle of repose of at most 40°, and a process for producing a molding, which comprises feeding the resin powder to an injection molding machine or extrusion molding machine, melting the resin powder, and injecting the resin melt into a mold.
摘要翻译:熔融成型用聚偏二氟乙烯树脂粉末,其平均粒径(D50)为80〜250μm,粒径为45μm以下的树脂粉末的比例为15.0%以下 ,粒径为355μm以上的树脂粉末的比例为10.0重量%以下,堆积密度为0.30〜0.80g / cm 3,休止角为40°以下, 用于制造模制品,其包括将树脂粉末进料到注射成型机或挤出成型机,熔化树脂粉末,并将树脂熔体注入模具中。