摘要:
The present invention is to provide a polyvinyl chloride (PVC) fiber for artificial hair. The PVC fiber is manufactured by melt spinning a PVC resin composition with a nozzle, wherein the nozzle has a nozzle hole having a diameter D and a land length L, and a nozzle leading portion having a cone angle, and wherein a ratio of L/D is 1-3, a height of the nozzle leading portion is at least 4 mm, and the cone angle is 20°-90°. The resulting PVC fiber has an arithmetic mean roughness of 0.18-0.38 μm and a maximum height of 0.5-3.5 μm along a longitudinal direction, specified by JIS B 0601.
摘要翻译:本发明提供一种人造毛发用聚氯乙烯(PVC)纤维。 PVC纤维通过使喷嘴具有PVC树脂组合物熔融纺丝制造,其中喷嘴具有直径D和平台长度L的喷嘴孔和具有锥角的喷嘴引导部分,其中L / D为1-3,喷嘴前端部的高度为4mm以上,锥角为20°〜90°。 得到的PVC纤维具有JIS B 0601规定的纵向的算术平均粗糙度为0.18-0.38μm,最大高度为0.5-3.5μm。
摘要:
The present invention is to provide a polyvinyl chloride (PVC) fiber for artificial hair. The PVC fiber is manufactured by melt spinning a PVC resin composition with a nozzle, wherein the nozzle has a nozzle hole having a diameter D and a land length L, and a nozzle leading portion having a cone angle, and wherein a ratio of L/D is 1-3, a height of the nozzle leading portion is at least 4 mm, and the cone angle is 20°-90°. The resulting PVC fiber has an arithmetic mean roughness of 0.18-0.38 μm and a maximum height of 0.5-3.5 μm along a longitudinal direction, specified by JIS B 0601.
摘要翻译:本发明提供一种人造毛发用聚氯乙烯(PVC)纤维。 PVC纤维通过使喷嘴具有PVC树脂组合物熔融纺丝制造,其中喷嘴具有直径D和平台长度L的喷嘴孔和具有锥角的喷嘴引导部分,其中L / D为1-3,喷嘴前端部的高度为4mm以上,锥角为20°〜90°。 得到的PVC纤维具有JIS B 0601规定的纵向的算术平均粗糙度为0.18-0.38μm,最大高度为0.5-3.5μm。
摘要:
Polyvinyl chloride fibers obtainable by molding a resin composition containing 100 parts by weight of a vinyl chloride resin, from 3 to 20 parts by weight of a compatible chlorinated vinyl chloride resin, from 10 to 30 parts by weight of a heat resistant chlorinated vinyl chloride resin, and from 0.1 to 10 parts by weight of a heat stabilizer into a fibrous form, the compatible chlorinated vinyl chloride resin having a chlorine content of from 57 to 64% by weight and an average degree of polymerization of from 450 to 800; and the heat resistant chlorinated vinyl chloride resin having a chlorine content of from 65 to 71% by weight and an average degree of polymerization of from 450 to 1,100, to a process of producing the same and to applications thereof.
摘要:
A polyvinyl chloride fiber which comprises a composition having 100 parts by weight of a vinyl chloride resin, from 3 to 20 parts by weight of a chlorinated vinyl chloride resin having a chlorine content of from 57.0 to 62.0% and an average polymerization degree of from 550 to 750, and from 5 to 50 parts by weight of a chlorinated vinyl chloride resin having a chlorine content of from 65.0 to 67.0% and an average polymerization degree of from 550 to 750.
摘要:
Polyvinyl chloride fibers obtainable by molding a resin composition containing 100 parts by weight of a vinyl chloride resin, from 3 to 20 parts by weight of a compatible chlorinated vinyl chloride resin, from 10 to 30 parts by weight of a heat resistant chlorinated vinyl chloride resin, and from 0.1 to 10 parts by weight of a heat stabilizer into a fibrous form, the compatible chlorinated vinyl chloride resin having a chlorine content of from 57 to 64% by weight and an average degree of polymerization of from 450 to 800; and the heat resistant chlorinated vinyl chloride resin having a chlorine content of from 65 to 71% by weight and an average degree of polymerization of from 450 to 1,100, to a process of producing the same and to applications thereof.
摘要:
The present invention is to provide a polyvinyl chloride (PVC) fiber for artificial hair. The PVC fiber is manufactured by melt spinning a PVC resin composition with a nozzle, wherein the nozzle has a nozzle hole having a diameter D and a land length L, and a nozzle leading portion having a cone angle, and wherein a ratio of L/D is 1-3, a height of the nozzle leading portion is at least 4 mm, and the cone angle is 20°-90°. The resulting PVC fiber has an arithmetic mean roughness of 0.18-0.38 μm and a maximum height of 0.5-3.5 μm along a longitudinal direction, specified by JIS B 0601.
摘要翻译:本发明提供一种人造毛发用聚氯乙烯(PVC)纤维。 PVC纤维通过使喷嘴具有PVC树脂组合物熔融纺丝制造,其中喷嘴具有直径D和平台长度L的喷嘴孔和具有锥角的喷嘴引导部分,其中L / D为1-3,喷嘴前端部的高度为4mm以上,锥角为20°〜90°。 得到的PVC纤维具有JIS B 0601规定的纵向的算术平均粗糙度为0.18-0.38μm,最大高度为0.5-3.5μm。
摘要:
[Problems] To provide a method of packing fiber for artificial hair, while suppressing generation of folding mark during packaging, transportation and storage and yet preserving preferable processability and hairdressing characteristics.[Means for Solving Problems] There is provided a method of packing fiber for artificial hair, characterized by packing the artificial hair fibers in a packaging container at a filling density of no lesser than 0.1 kg/l and no more than 0.8 kg/l. Further in the packing method, the pressure of the packed artificial hair fibers applied to the top face of the packaging container is adjusted to no lesser than 0.1 kPa and no more than 8.0 kPa.
摘要:
The present invention is to provide a vinyl chloride fiber formed with a vinyl chloride resin composition containing (a) 100 parts by mass of a vinyl chloride resin, (b) 0.2-5.0 parts by mass of a hydrotalcite thermal stabilizer and (c) 0.2-10.0 parts by mass of a epoxy compound. The addition of (c) 0.2-10.0 parts by mass of the epoxy compound to the vinyl chloride resin composition improves a dispersion of the hydrotalcite thermal stabilizer so that a long-run and stable melt spinning is achieved. The vinyl chloride fiber manufactured shows a little color change when the fiber is curled at a curling process.