    POLYPROPYLENE BASED COMPOSITION WITH IMPROVED PAINTABILITY
    2.
    发明申请
    POLYPROPYLENE BASED COMPOSITION WITH IMPROVED PAINTABILITY 有权

    公开(公告)号：US20210253838A1

    公开(公告)日：2021-08-19

    申请号：US17269217

    申请日：2019-08-23

    Applicant: BOREALIS AG

    Inventor： Jingbo Wang ,  Friedrich Berger ,  Daniela Mileva ,  Georg Grestenberger ,  Markus Gahleitner

    IPC: C08L23/12

    Abstract: The present invention relates to a polypropylene based composition comprising:(A) from 40.0 to 85.0 wt % of a heterophasic propylene copolymer having a content of xylene cold soluble (XCS) fraction in the range of 15 wt % to 35 wt %, based on the total weight of the heterophasic propylene copolymer;(B) from 5.0 to 15.0 wt % of a terpolymer of propylene with ethylene and 1-butene comonomer units having a melting temperature Tm as measured in differential scanning calorimetry (DSC) of less than 140° C.; (C) from 5.0 to 25.0 wt % of an ethylene copolymer with alpha-olefin comonomer units having from 4 to 12 carbon atoms with a density of from 850 kg/m3 to 900 kg/m3; and(D) from 5.0 to 25.0 wt % of an inorganic filler, wherein the amounts of components (A), (B), (C), and (D) are all based on the total weight amount of the polypropylene based composition, said polypropylene based composition having a melt flow rate (MFR2) as measured at 230° C. and 2.16 kg load in accordance with ISO 1133 in the range of 2.0 g/10 min to 20 g/10 min, an article comprising said polypropylene based composition and the use of said terpolymer (B) for reducing the paint adhesion failure of an article comprising said polypropylene based composition.

    NOVEL POLYPROPYLENE COMPOSITIONS WITH LOW FOGGING
    5.
    发明申请
    NOVEL POLYPROPYLENE COMPOSITIONS WITH LOW FOGGING 审中-公开

    公开(公告)号：US20190300686A1

    公开(公告)日：2019-10-03

    申请号：US16308199

    申请日：2017-06-20

    Applicant: BOREALIS AG

    Inventor： Jingbo Wang ,  Claudia Kniesel ,  Minna Aarnio-Winterhof ,  Karlheinz Friedrich ,  Friedrich Berger

    IPC: C08L23/12

    Abstract: Polypropylene composition comprising (A) 60 to 95 wt % of a heterophasic polypropylene (HECO) comprising 10 to 30 wt % of dispersed phase with the dispersed phase having a comonomer content of 30 to 45 wt % and the HECO having a melt flow rate MFRPP in the range of 12 to 200 g/10 min and being prepared in the presence of a Ziegler Natta catalyst (ZN-C), (B) 0 to 15 wt % of one or more elastomers, (C) 5 to 20 wt % of at least one filler wherein the polypropylene composition fulfils inequation (1) fogging≤0.02 MFRComp+0.3. The composition allows for a well-balanced combination of a good impact/stiffness balance, a good scratch resistance, low VOC and FOG emissions and remarkable good fogging values.

    MULTILAYER POLYPROYLENE FILM
    8.
    发明申请
    MULTILAYER POLYPROYLENE FILM 有权

    公开(公告)号：US20210362479A1

    公开(公告)日：2021-11-25

    申请号：US17253872

    申请日：2019-07-22

    Applicant: BOREALIS AG

    Inventor： Markus Gahleitner ,  Jingbo Wang ,  Friedrich Berger ,  Manfred Gruenberger

    IPC: B32B27/08 ,  B32B27/32 ,  B32B27/30 ,  C08F210/06

    Abstract: Multilayer film comprising at least a skin layer, a core layer and an inner layer, the skin layer comprising a homo polypropylene or a random propylene ethylene copolymer including up to 2.5 wt.-% units derived from ethylene, the homopolypropylene or the random propylene ethylene copolymer having a MFR2 (ISO1 133, 230° C.) of 2.0 to 20 g/10 min and a melting temperature (Tm) of above 148° C. measured by DSC according to ISO 11357-3:1999 and a scan rate of 10° C./min; the core layer comprising a mixture obtainable by melt blending 20 to 100 wt.-% of a random heterophasic copolymer and 0 to 80 wt.-% of styrene based TPE, whereby the random heterophasic copolymer has a melting temperature (Tm) of 134° C.-148° C. measured by DSC according to ISO 11357-3:1999 and a scan rate of 10° C./min and includes a propylene ethylene copolymer rubber; and whereby the styrene based TPE has a styrene content of from 5 to 20 wt.-%, and the inner layer comprising a random propylene ethylene copolymer having a melting temperature (Tm) from 132° C. to 144° C. measured by DSC according to ISO 11357-3:1999 and a scan rate of 10° C./min, wherein the multilayer film is free of phthalic acid esters as well as decomposition products thereof.