公开(公告)号：US20170073798A1

公开(公告)日：2017-03-16

申请号：US15125477

申请日：2015-02-06

申请人： Doosan Infracore Co., Ltd.

发明人： Young-Kyu JU ,  Ki-Hwan JUNG ,  Jong-Kwon CHUNG ,  Sik YANG ,  Jae-Hyoung HWANG ,  Dong-Seob SHIM ,  Sang-Beom KIM

IPC分类号： C22C37/10 ,  C22C37/06 ,  C22C33/08 ,  G01N25/00 ,  B22D25/02 ,  F01N13/14 ,  G01N33/20 ,  H01J49/26 ,  C22C37/04 ,  B22D17/00

CPC分类号： C22C37/10 ,  B22D17/00 ,  B22D25/02 ,  C21C1/105 ,  C21D5/00 ,  C21D2211/004 ,  C21D2211/005 ,  C21D2211/009 ,  C22C33/04 ,  C22C33/08 ,  C22C37/04 ,  C22C37/06 ,  F01N13/14 ,  F01N2510/02 ,  G01N25/00 ,  G01N33/206 ,  H01J49/26

摘要： Heat resistant spheroidal graphite cast iron having an improved high temperature tensile strength includes carbon (C) in a range of 3.2-3.4 wt %, silicon (Si) in a range of 4.3-4.8 wt %, manganese (Mn) in a range of 0.2-0.3 wt %, molybdenum (Mo) in a range of 0.8-1.0 wt %, vanadium (V) in a range of 0.4-0.6 wt %, chrome (Cr) in a range of 0.2-0.4 wt %, niobium (Nb) in a range of 0.2-0.4 wt %, inevitable impurities, and a remainder of iron (Fe) based on a total weight of the heat resistant spheroidal graphite cast iron. The heat resistant spheroidal graphite cast iron further includes barium (Ba) in a range of 0.0045-0.0075 wt %. A content ratio of chrome (Cr) and barium (Ba) (Cr/Ba) is in a range from about 26 to about 89.

摘要翻译： 具有改善的高温拉伸强度的耐热球墨铸铁包括在3.2-3.4重量％范围内的碳（C），在4.3-4.8重量％范围内的硅（Si），在 0.2-0.3重量％，0.8-1.0重量％的钼（Mo），0.4-0.6重量％的钒（V），0.2-0.4重量％的铬（Cr），铌（ Nb）在0.2-0.4重量％的范围内，不可避免的杂质，剩余的铁（Fe）基于耐热球墨铸铁的总重量。 耐热球墨铸铁还包括0.0045-0.0075重量％范围内的钡（Ba）。 铬（Cr）和钡（Ba）（Cr / Ba）的含量比在约26至约89的范围内。

公开(公告)号：US20170016098A1

公开(公告)日：2017-01-19

申请号：US15120651

申请日：2015-02-06

申请人： DOOSAN INFRACORE CO., LTD.

发明人： Ki-Hwan JUNG ,  Young-Kyu JU ,  Jong-Kwon CHUNG ,  Jae-Hyoung HWANG ,  Sik YANG ,  Dong-Seob SHIM ,  Sang-Beom KIM

IPC分类号： C22C37/10 ,  F01N13/10 ,  C22C37/04

CPC分类号： C22C37/10 ,  C22C37/04 ,  F01N13/10 ,  F01N13/16 ,  F01N2510/08

摘要： A spheroidal graphite cast iron for a component of an engine exhaust system includes carbon ranging from about 3.0 wt % to about 3.4 wt %, silicon ranging from about 4.2 wt % to about 4.5 wt %, manganese ranging from about 0.1 wt % to about 0.3 wt %, sulfur ranging from about 0.002 wt % to about 0.01 wt %, phosphorous in a range equal to or less than about 0.05 wt %, magnesium ranging from about 0.035 wt % to about 0.055 wt %, molybdenum ranging from about 0.9 wt % to about 1.2 wt %, nickel ranging from about 0.2 wt % to about 0.5 wt %, vanadium ranging from about 0.4 wt % to about 0.6 wt %, niobium ranging from about 0.1 wt % to about 0.4 wt %, cerium ranging from about 0.005 wt % to about 0.01 wt %, aluminum ranging from about 0.003 wt % to about 0.007 wt %, and a remainder of iron.

摘要翻译： 用于发动机排气系统的组件的球墨铸铁包括约3.0重量％至约3.4重量％的碳，约4.2重量％至约4.5重量％的硅，约0.1重量％至约0.3重量％的锰 重量％，约0.002重量％至约0.01重量％的硫，约等于或小于约0.05重量％的磷，约0.035重量％至约0.055重量％的镁，约0.9重量％ 至约1.2重量％的镍，约0.2重量％至约0.5重量％的镍，约0.4重量％至约0.6重量％的钒，约0.1重量％至约0.4重量％的铌，约0.005重量％ wt％至约0.01wt％，铝范围为约0.003wt％至约0.007wt％，余量为铁。