1.发明授权Molten aluminum alloy processing method and flux for molten aluminum alloy processing 失效熔融铝合金加工方法和熔融铝合金加工助熔剂公开(公告)号：US06936089B2
公开(公告)日：2005-08-30
申请号：US10263842
申请日：2002-10-04
CPC分类号： C22B21/062 , C22B9/10 , C22B21/0092 , Y02P10/218
摘要： A molten aluminum alloy processing method is intended use sludge produced by the zinc phosphate treatment of structures including those of aluminum alloys effectively as a flux for molten aluminum alloy processing. The flux contains 3 to 30% by mass fluorine-equivalent metal fluorides, 40 to 90% by mass metal phosphates (8 to 18% by mass P) and 50% by mass or below inorganic salts. The sum of contents of the inorganic salts and metal phosphates is 90% by mass or below.
摘要翻译： 熔融铝合金加工方法是使用通过磷酸锌处理生成的污泥作为熔融铝合金加工助熔剂，将包括铝合金的结构在内的结构有效地利用。 助熔剂含有3〜30质量％的氟当量金属氟化物，40〜90质量％的金属磷酸盐（8〜18质量％P）和50质量％以下的无机盐。 无机盐和金属磷酸盐的含量之和为90质量％以下。
-
公开(公告)号：US09574258B2
公开(公告)日：2017-02-21
申请号：US13403389
申请日：2012-02-23
摘要： An aluminum-alloy sheet includes 0.10 to 0.40 mass % of Si, 0.35 to 0.80 mass % of Fe, 0.10 to 0.35 mass % of Cu, 0.20 to 0.80 mass % of Mn, and 1.5 to 2.5 mass % of Mg, the balance being Al and unavoidable impurities, wherein a content ratio (Si/Fe) of the Si to the Fe is 0.75 or less, the area fraction of Mg2Si intermetallic compound grains having a maximum length of 1 μm or more is 0.10% or more in a region of a section of the aluminum-alloy sheet, the region being a central region in the thickness direction of the aluminum-alloy sheet, and the aluminum-alloy sheet has a proof stress of 225 to 270 N/mm2 after having been baked at 270° C. for 20 seconds.
摘要翻译： 铝合金板包括Si：0.10〜0.40质量％，Fe：0.35〜0.80质量％，Cu：0.10〜0.35质量％，Mn：0.20〜0.80质量％，Mg：1.5〜2.5质量％ Al和不可避免的杂质，其中Si与Fe的含量比（Si / Fe）为0.75以下，在区域的最大长度为1μm以上的Mg2Si金属间化合物粒子的面积分率为0.10％以上 铝合金板的厚度方向上的中心区域为铝合金板的截面，铝合金板在烧成后为270〜270N / mm 2。 ℃20秒。
-
公开(公告)号：US09546411B2
公开(公告)日：2017-01-17
申请号：US13403370
申请日：2012-02-23
摘要： An aluminum-alloy sheet includes 0.10 to 0.40 mass % of Si, 0.35 to 0.80 mass % of Fe, 0.10 to 0.35 mass % of Cu, 0.20 to 0.80 mass % of Mn, and 1.5 to 2.5 mass % of Mg, the balance being Al and unavoidable impurities, wherein a content ratio (Si/Fe) of the Si to the Fe is 0.75 or less, the solute Mn content is 0.12 to 0.20 mass %, and the aluminum-alloy sheet has a proof stress of 225 N/mm2 or more after having been baked at 270° C. for 20 seconds.
摘要翻译： 铝合金板包括Si：0.10〜0.40质量％，Fe：0.35〜0.80质量％，Cu：0.10〜0.35质量％，Mn：0.20〜0.80质量％，Mg：1.5〜2.5质量％ Al和不可避免的杂质，其中Si与Fe的含量比（Si / Fe）为0.75以下，溶质Mn含量为0.12〜0.20质量％，铝合金板的抗应力为225N / 在270℃下烘烤20秒后，mm2以上。
-
公开(公告)号：US20120227871A1
公开(公告)日：2012-09-13
申请号：US13403389
申请日：2012-02-23
摘要： An aluminum-alloy sheet includes 0.10 to 0.40 mass % of Si, 0.35 to 0.80 mass % of Fe, 0.10 to 0.35 mass % of Cu, 0.20 to 0.80 mass % of Mn, and 1.5 to 2.5 mass % of Mg, the balance being Al and unavoidable impurities, wherein a content ratio (Si/Fe) of the Si to the Fe is 0.75 or less, the area fraction of Mg2Si intermetallic compound grains having a maximum length of 1 μm or more is 0.10% or more in a region of a section of the aluminum-alloy sheet, the region being a central region in the thickness direction of the aluminum-alloy sheet, and the aluminum-alloy sheet has a proof stress of 225 to 270 N/mm2 after having been baked at 270° C. for 20 seconds.
摘要翻译： 铝合金板包括Si：0.10〜0.40质量％，Fe：0.35〜0.80质量％，Cu：0.10〜0.35质量％，Mn：0.20〜0.80质量％，Mg：1.5〜2.5质量％ Al和不可避免的杂质，其中Si与Fe的含量比（Si / Fe）为0.75以下，在区域的最大长度为1μm以上的Mg2Si金属间化合物粒子的面积分率为0.10％以上 铝合金板的厚度方向上的中心区域为铝合金板的截面，铝合金板在烧成后为270〜270N / mm 2。 ℃20秒。
-
公开(公告)号：US20120227870A1
公开(公告)日：2012-09-13
申请号：US13403370
申请日：2012-02-23
摘要： An aluminum-alloy sheet includes 0.10 to 0.40 mass % of Si, 0.35 to 0.80 mass % of Fe, 0.10 to 0.35 mass % of Cu, 0.20 to 0.80 mass % of Mn, and 1.5 to 2.5 mass % of Mg, the balance being Al and unavoidable impurities, wherein a content ratio (Si/Fe) of the Si to the Fe is 0.75 or less, the solute Mn content is 0.12 to 0.20 mass %, and the aluminum-alloy sheet has a proof stress of 225 N/mm2 or more after having been baked at 270° C. for 20 seconds.
摘要翻译： 铝合金板包括Si：0.10〜0.40质量％，Fe：0.35〜0.80质量％，Cu：0.10〜0.35质量％，Mn：0.20〜0.80质量％，Mg：1.5〜2.5质量％ Al和不可避免的杂质，其中Si与Fe的含量比（Si / Fe）为0.75以下，溶质Mn含量为0.12〜0.20质量％，铝合金板的抗应力为225N / 在270℃下烘烤20秒后，mm2以上。
-
-
-
-