公开(公告)号：US20140377555A1

公开(公告)日：2014-12-25

申请号：US14372507

申请日：2013-02-21

申请人： Kureha Corporation

发明人： Kotaku Saigusa

IPC分类号： D01F8/14 ,  B29C47/00 ,  D01F8/10

CPC分类号： D01F8/14 ,  B29C48/0022 ,  B29C48/022 ,  B29K2067/043 ,  B29K2067/046 ,  C09K8/035 ,  C09K8/516 ,  C09K2208/08 ,  D01F8/10 ,  Y10T428/2907 ,  Y10T428/2929 ,  Y10T428/2931

摘要： A water-disintegrable composite fiber comprising: a phase containing a polyglycolic acid resin; and a phase containing another resin having a mass loss of 25% or greater after immersion for 7 days in 80° C. pure water and having a glass transition temperature Tg of 25° C. or higher; the two phases extending continuously in the lengthwise direction; and the fiber having a side surface in which a region formed from the phase containing the polyglycolic acid resin is 50% or less in terms of area ratio, and a cross section in which a region formed from the phase containing the polyglycolic acid resin is 50% or greater in terms of area ratio.

摘要翻译： 一种水崩解复合纤维，包括：含有聚乙醇酸树脂的相; 以及在80℃纯水中浸渍7天后具有25℃以上的玻璃化转变温度Tg为25℃以上的质量损失为25％以上的另一种树脂的相。 两相沿长度方向连续延伸; 并且所述纤维具有侧面，其中由含有所述聚乙醇酸树脂的相形成的区域的面积的面积比为50％以下，从由所述聚乙醇酸树脂的相形成的区域为50的截面 ％以上的面积比。

公开(公告)号：US20150247021A1

公开(公告)日：2015-09-03

申请号：US14432840

申请日：2013-10-09

申请人： KUREHA CORPORATION

发明人： Kotaku Saigusa ,  Satoru Suzuki

IPC分类号： C08K3/36 ,  C08K3/34 ,  C08J3/20

CPC分类号： C08K3/36 ,  C08J3/203 ,  C08J2367/04 ,  C08K3/34 ,  C08L67/04

摘要： A polyglycolic acid resin (PGA) composition which can be used as a packaging material or a material for a drilling downhole tool (member), the composition containing from 30 to 90 mass % of a PGA and from 70 to 10 mass % of an inorganic filler, wherein the percentage of mass loss of the PGA after immersion in water for 3 hours at a temperature of 120° C. is at least 20% and preferably at least 25%, and the deflection temperature under load is 120° C. or higher; and a method for producing a PGA composition, the method including a step of melt-kneading using an extruder.

摘要翻译： 可用作包装材料的聚乙醇酸树脂（PGA）组合物或用于钻井井下工具（构件）的材料，该组合物含有30〜90质量％的PGA和70〜10质量％的无机 填料，其中在120℃的温度下浸渍在水中3小时后的PGA的质量损失百分比为至少20％，优选至少25％，负载下的挠曲温度为120℃，或 更高; 以及PGA组合物的制造方法，该方法包括使用挤出机进行熔融混炼的工序。